Abstract
An Fe$_{49}$ Co$_{49}$ V$_2$alloy is annealed in thermal annealing furnace at 50$0^{\circ}C$, 75$0^{\circ}C$, 80$0^{\circ}C$, and 90$0^{\circ}C$. Annealed samples were cooled in air. The magnetostriction is measured by using a Michelson laser interferometer. Receiving the feedback signal of interference, a mirror attached to piezoelectric transducer (PZT) maintains the optical path length (OPL) between two arms of laser interferometer relatively constant. The feedback voltage is calibrated to the OPL variation. A magnetostriction of 2$\times$10$^{-6}$ at H = 60 Oe increases up to 33.68$\times$10$^{-6}$ at an annealing temperature of 90$0^{\circ}C$, suggesting that the magnetostrictive characteristics are improved by the microstructural modification.
Fe$_{49}$ Co$_{49}$ V$_2$합금을 50$0^{\circ}C$, 75$0^{\circ}C$, 80$0^{\circ}C$ 및 90$0^{\circ}C$의 furnace에서 열처리한 후, 공냉조건으로 냉각하여 시료를 제작하였다. Michelson 레이저 간섭계를 이용하여 시료의 자기변형을 측정하였다 시료의 자기변형은 간섭계의 한쪽 팔에 piezoelectric transducer(PZT)를 부착하여 간섭계의 두 팔 사이의 상대적 광경로를 일정하게 유지하였으며 궤환회로의 전압을 광경로의 변화(자기변형)로 환산하였다. 시료를 90$0^{\circ}C$의 furnace에서 열처리한 후, H = 60 Oe에서 Fe$_{49}$ Co$_{49}$ V$_2$합금의 자기변형을 측정한 결과열처리 전 2$\times$$10^{-6}$ 에서 33.68$\times$$10^{-6}$ 가지 증가하였다. 이것은 시료의 미세구조가 변화되어 자기특성이 개선된 것으로 생각된다.