Magnetic Properties in Alternating Magnetic Field for the Sintered Ee-l7Cr-2M(M=Si, Nb, Mo) Alloys

Fe-l7Cr-2M(M=Si, Nb, Mo)합금 분말 소결체의 교류 자기 특성

Fe-l7Cr-2M(M=Si, Nb, Mo) alloy powder was prepared by plasma electrode rotating atomizer and than the alloy powder was formed and sintered. The particle shape of the Fe-l7Cr-2M(M=Si, Nb, Mo) alloy power is spherical. The saturation magnetization of the sintered Fe-17Cr-2Mo and Fe-l7Cr-2Nb alloy are 155 emu/g. The saturation magnetization of the sintered Fe-l7Cr-2Si alloy is less than that of the sintered Fe-l7Cr-2Mo and Fe-l7Cr-2Nb alloy. The amplitude relative permeability of the sintered Fe-l7Cr-2M(M=Si, Nb, Mo) alloy has the maximum value in the range of 3∼5 Oe applied field at forming pressure 12 ton/cm$^2$, sintering temperature 1200$^{\circ}C$, and frequency 1 kHz. Power loss of the sintered Fe-l7Cr-2Nb alloy is 40 mW/cc at applied field, H$\sub$a/=5 Oe, and frequency, f=1 kHz. The power loss of the sintered Fe-l7Cr-2Nb alloy is a half of that of the sintered Fe-l7Cr-2Si and Fe-l7Cr-2Mo alloy.

Fe-l7Cr-2M(M=Si, Nb, Mo)합금분말을 Electrode Rotating Atomizer로 제조한 후 성형하여 소결한 시편의 첨가원소, 성형 압력 및 소결온도 에 따른 교류자기특성의 변화를 체계적으로 조사하였다 제조된 Fe-l7Cr-2M(M=Si, Nb, Mo) 합금분말의 형상은 구형이며, 포화자화값은 Mo와 Nb을 첨가한 Fe-l7Cr-2Mo과 Fe-l7Cr-Nb의 경우 약 155 emu/g로 Si을 첨가한 경우보다 크다. 성형압력 12 ton/$cm^2$, 소결온도 1200 $^{\circ}C$에서 제조된 Fe-l7Cr-2M(M=Si, Nb, Mo)합금분말 소결체의 진폭비 투자율은 주파수, f=1 kHz에서 3~5 Oe의 인가자장 범위에서 가장 크다. 전력손실은 인가자장 H$_{a}$ =5 Oe, 주파수 f=1 kHz에서 Fe-l7Cr-2Nb 경우 40 mW/cc로 Si이나 Mo를 첨가한 경우 보다 약 1/2값을 나타낸다.