Abstract
Influence of seed addition on the mullite synthesis was investigated from mixture powders of kaolin and aluminium trihydroxide which contain various $Al_2O_3$/SiO_2$ ratio (silica rich, stoichiometric, alumina rich). The flexural strength increases with the increase of the mullite-seed content in case of silica rich and stoichiometric mullite, but flexural strength decreases with the increase of the mullite-seed content in case of alumina rich mullite. Microstructural investigation revealed that aspect ratio of mullite grains increased with higher alumina content, along with lower sintered density. Mullite contents of specimens are increased with seed content regardless of $Al_2O_3$/SiO_2$ ratio of the mixture composition.
kaolin과 수산화알루미늄을 이용하여 mullite를 합성하는데 있어서 출발원료의 조성을 silica rich, stoichiometric, alumina rich 조성으로 준비하여 각각의 원료로부터 mullite를 합성할 때 mullite-seed가 미치는 영향을 연구하였다. 그 결과 silica rich 조성과 stoichiometric 조성에서는 mullite-seed의 첨가량이 증가할수록 꺾임강도값이 증가하며, alumina rich 조성에서는 mullite-seed의 첨가량이 증가할수록 꺾임강도값은 감소하는 경향을 보였다. 같은 양의 mullite-seed를 첨가했을 때 미세구조는 alumina 첨가 함량이 증가할수록 치밀도가 감소하고, aspect ratio는 증가하는 경향을 나타내었다. 순도면에서는 mullite정량결과 모든 조성에서 mullite-seed의 첨가량이 많을수록 합성된 mullite 결정상의 함량이 증가하는 경향을 보였다.