Abstract
Quantitative analysis of iron ore sinter consisting of hematite, magnetite, calcium ferrite and slag was investigated by X-ray internal standard method. After selecting NaF and $SiO_2$as internal standard materials, the calibration curves were determined and were applied to quantitative analysis of the internal standard method. Calcium ferrite was identified as a solid solution of CaO.$2Fe_2$$O_3$with 7 wt% and 3 wt% solubility of $AI_2$$O_3$and $SiO_2$, respectively. The maximum deviation of quantitative analysis of synthetic iron ore was about $\pm$5 wt%. The contents of each mineral calculated in industrial sinter were 27~40 wt% of hematite, 20~30 wt% of magnetite, 22~33 wt% of calcium ferrite and 10~20 wt% of slag.
소결광을 구성하는 광물상(hematite, magnetite, calcium ferrite, slag)들을 X선 내부표준법을 이용하여 정량분석을 하였다. 분석에는 표준물질로 NaF와 SiO$_2$를 선택하여 교정곡선을 작성하여 내부표준법에 적용하였다. 소결광내에 존재하는 calcium ferrite는 순수 CF(CaO.$Fe_2$$O_3$에 X선 회절피크는 나타나지 않았으며, 순수 $CF_2(CaO.$2Fe_2$$O_3$)에 근접하였으나 CF2에 소량의 $Al_2$$O_3$와 $SiO_2$가 고용된 4원계($Fe_2$$O_3$-CaO-$AI_2$$O_3$-$SiO_2$)에 보다 더 근접한 것으로 나타났다. 합성소결광의 정량분석은 두 표준물질 모두 상대오차가 $\pm$5 wt% 내에서 일치하였다. 실제 소결광의 정량분석결과 hematite는 27~40 wt%, magnetite는 20~30 wt%, calcium ferrite 22~33 wt%, slag 10~20 wt% 범위에서 분포하였다.