Abstract
The structural, electrical and etching characteristics of Al alloy thin film with low impurity concentrations AlNd deposited by using do magnetron sputtering deposition are investigated for the applications as gate bus line in the TFt-LCD panel. And ITO thin film was deposited on AlNd, then the contact resistance was measured by Kelvin resistor. The deposited thin films show the decrease of resistivity and the increase of grain size after the RTA at $300^{\circ}C$ for 20 min. Moreover, the resistivity of AlNd does not show appreciable grain size dependence after RTA. It is concluded that the decrease of resistivity after RTA is due to the increase of grain size. The annealed AlNd is found to be hillock free. The etching profiles of AlNd was good and the minimun contact resistance was about $110\;{\mu\Omega}cm$. Calculation results reveal that the AlNd (2wt.%) thin film can be applicable to 25" SXGA class TFT-LCD panels.
TFT-LCD(thin film transistor-liquid crystal display) 패널의 데이터 배선 재료로 사용하기 위하여 AlNd(2 wt%)의 Al합금 박막을 dc 마그네트론 스퍼터링 방법으로 유리 기판에 증착하여 열처리전과 열처리후의 구조적, 전기적, 식각 박막 특성을 조사하였다. 또한 증착한 박막을 식각하여 그 특성을 조사하였고, ITO를 증착하여 AlNd과의 접촉 저항을 Kelvin resistor를 사용하여 측정하였다. 증착된 박막을 $350^{\circ}C$에서 20분간 열처리 하였을때 AlW박막은 비저항이 감소하였고 약 $4\;{\mu\Omega}cm$의 아주 좋은 비저항 특성을 보였다. 주사전자 현미경(SEM)과 원자힘현미경(AFM)으로 표면을 분석한 결과 좋은 힐록방지 특성을 보임을 알 수 있었다. AlNd의 식각 특성은 아주 좋게 나타났고, ITO와 AlNd의 최저 접촉저항값은 약 $110\;{\mu\Omega}cm$이었다. 측정된 특성들을 바탕으로 AlNd(2 wt.%) 박막의 적용 가능성을 해상도와 화면 크기 측면에서 살펴보았을 때, 25인치 SXGA급 패널에 적용 가능함을 알 수 있었다.