Study on the Growth of Soybean and Corn in Artificial Media

인공배지를 이용한 옥수수와 콩의 생육시험 연구

For the recycling of sludge as soil conditioner, the firing technology in pottery industry was applied to the sludge treatment, and produced artificial media with many voids. To produce artificial media using sludge, chabazite and lime were used as additives, and the mixture of sludge and additives was thermally treated in the firing kiln at about $800{\sim}1,100^{\circ}C$ for about ten minutes. The effect of mixed artificial media into upland soil was investigated through the crop growth experiment and the physical & chemical characteristics of the mixed soils were analysed. The pH of artificial media was higher than that of the control soils. After the plant growth experiment, artificial media plots almost contained more CEC, OM, TN, TP and $AV.P_2O_5$ than upland soil plots. From the growth analysis, growth of soybean and corn in the artificial media plots was better than that in the original upland soil plots. The yield of soybean and corn in the artificial media plots were about 46kg/10a, 194kg/10a, respectively, which is higher than that in the control. Heavy metals in the artificial media plots were lower than the standard regulation. Therefore, the artificial media produced from sludge can be mixed into farmland, and crop production can be increased additionally.

슬러지를 토양개량제로 재활용하기 위하여 슬러지 처리에 요업소성 공법을 적용하여 다공극성의 인공배지를 생산하였다. 슬러지를 이용해 인공배지를 생산하기 위하여 자바사이트와 석회를 첨가재로 사용하였으며, 첨가재와 슬러지를 혼합한 시료를 $800{\sim}1,100^{\circ}C$의 고온으로 열처리하였다. 비교 밭 토양에 인공배지를 혼합한 후, 혼합토양의 물리${\cdot}$화학성을 분석하였고, 작물 생육 시험을 통하여 인공배지 혼합에 따른 영향을 조사${\cdot}$분석하였다. 인공배지의 pH는 비교 밭 토양구보다 높았다. 작물 생장 시험 후 비교 밭 토양 보다 인공배지 처리구에서 대부분 CEC, OM, TN, TP 및 $AV.P_2O_5$가 높게 나타났다. 작물 생장 시험 결과 인공배지 처리구에서 콩과 옥수수의 생육 상태가 비교 밭 토양구에서 보다 좋은 것으로 나타났다. 또한 콩과 옥수수의 수확량도 각각 약 46kg/10a, 194kg/10a 정도 인공배지 처리구에서 높게 나타났다. 인공배지 처리구의 중금속 함량은 모든 처리구에서 기준치보다 낮게 나타났다. 따라서 슬러지로 만든 인공배지를 일반 밭 토양에 혼합하여 작물을 재배하여도 문제가 없을 것으로 판단된다.