Measurement of Absorbed Dose for High Energy Electron using $CaSO_4$:Tm-PTFE TLD

$CaSO_4$:Tm-PTFE TLD를 이용한 고에너지 전자선의 흡수선량 측정

  • Park, Myeong-Hwan (Dept. of Radiologic Technology, Taegu Health College) ;
  • Kim, Do-Sung (Devision of Science Education, Taegu University) ;
  • Doh, Sih-Hong (Dept. of Physics, Pukyong National University) ;
  • Kim, Wan (Dept. of Physics, Kyungpook National University) ;
  • Kang, Hee-Dong (Dept. of Physics, Kyungpook National University)
  • 박명환 (대구보건대학 방사선과) ;
  • 김도성 (대구대학교 과학교육학부) ;
  • 도시홍 (부경대학교 물리학과) ;
  • 김완 (경북대학교 물리학과) ;
  • 강희동 (경북대학교 물리학과)
  • Published : 2001.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, the highly sensitive $CaSO_4$:Tm-PTFE TLDs has been fabricated for the purpose of measurement of high energy electron. $CaSO_4$:Tm phosphor powder was mixed with polytetrafluoroethylene(PTFE) powder and moulded in a disk type(diameter 8.5mm, thickness $90mg/cm^2$) by cold pressing. The batch uniformities were average deviation 3.1%. The TLDs were applied to measurement of absorbed dose distribution for high energy electron, the ranges were determined to be $R_{100}=14.5mm$, $R_{50}=24.1mm$ and $R_p=31.8mm$, respectively. The beam flatness were 4.5% as the variation of dose relative to the central axis over the central 80% of the field size at a maximum dose depth in a plane perpendicular to the central axis.

$CaSO_4$:Tm 열형광체 분말 20wt%를 PTFE와 혼합하여 직경 8.5mm, 두께 $90mg/cm^2$로 압축 성형한 후 중합하여 디스크 형태의 $CaSO_4$:Tm-PTFE TLD소자를 제작하였다. $^{60}Co$ 원격조사장치를 이용하여 0.5Gy의 $\gamma$-선을 조사한 TLD 소자의 균일성은 3.1%로 우수하였다. 이 중에서, 선별한 TLD를 이용하여 고에너지 전자선에 대한 polystyrene 팬톰에서의 흡수선량 분포를 측정하여 최대선량깊이, 50%선량깊이 및 실용비정의 값을 구할 수 있었으며, 조사야 내의 beam 평탄도는 4.5%로 나타났다. 이들 값은 dosimetry system으로 측정한 결과와 비교하여 다소 증가하는 경향을 나타내었다.