Sintering and dielectric properties of $(Pb,La)TiO_3$ powder prepared by hydrothermal method

수열법에 의해 합성된$(Pb,La)TiO_3$분말의 소결 및 유전특성

The $[(Pb_{1-x}$La_{2x/3})TiO_3$, X=0.2] powder was synthesized by the hydrothermal method, and their sintering and dielectric properties according to Mn additive were examined. The relative density of sintered PLT specimen at $1150^{\circ}C$ for 5 hrs with Mn 0.02 mol% additive was 96.7%. The dielectric properties of sintered PLT specimen were changed by content of Mn and increacement of sintering temperature. Dissipation factor was improved by increasing of measuring temperature. Curie temperature of sintered PLT specimens was decreased with increasing of Mn additive.

수열법으로 $(Pb_{1-x}$La_{2x/3})TiO_3$(PLT, X=0.2) 분말을 합성한 후, $MnO_2$를 0.00~0.02 mol% 첨가하여 그에 따른 소결거동 및 유전특성을 조사하였다. PLT 소결체의 상대밀도는, Mn이 0.02 mol% 첨가되고 $1150^{\circ}C$에서 5시간 소결할 경우 96.7%이였다. PLT의 유전특성은, $MnO_2$의 함량과 소결온도의 변화에 따라 변하였다. Mn의 첨가나 소결온도의 증가시 유전손실값은 측정온도의 증가에 따라 증가되었다. Curie 온도는 Mn 첨가량의 증가와 더불어 감소하였으며, Mn이 0.02 mol% 첨가될 경우, 첨가하지 않은 경우보다 60~$70^{\circ}C$ 감소하였다.