Fabrication and Properties of ferroelectric BST thin films prepared by sol-gel method (II) - effect of ultrasound on properties of thin film

졸-겔법에 의한 강유전 BST 박막의 제조 및 특성(II) - 초음파의 효과

  • 이진홍 (경북대학교 무기재료공학과) ;
  • 박병옥 (경북대학교 무기재료공학과) ;
  • 이승엽 (경북대학교 무기재료공학과)
  • Published : 2001.12.01

Abstract

($Ba_{0.7}Sr_{0.3})TiO_3$thin films were perpared on ITO-coated glass substrate by spin-coating method. The sol was sonicated in an ultrasonic bath to promote homogenization and the results were compared with untreated case. By application of the sonication process, crystallization temperatures of films were reduced, microstructers of films were more uniform and denser and the surface roughness of the films was lower from 8.4nm to 5.6nm. In addition, optical transmittances and electrical properties of films prepraed from sonicated sol were superior to those of films from untreated.

($Ba_{0.7}Sr_{0.3})TiO_3$박막을 ITO-coated glass 기판위에 spin-coating법으로 제조하였다. 제조된 용액을 초음파 bath 내에서 초음파 처리하여 균일화를 촉진시킨 후 박막을 제조하여 초음파 처리하지 않은 용액으로 제조한 박막과의 비교를 통하여 초음파 효과를 알아보았다. 용액의 초음파 처리로 박막의 결정화 온도를 다소 낮추었으며 박막의 표면이 보다 균일하고 치밀화되었고 거칠기도 8.4nm에서 5.6nm로 더 낮아졌다. 그리고 박막의 투광성 및 전기적 특성 또한 용액의 초음파 처리로 인하여 향상되었다.

Keywords