The hydration resistance improvement of MgO ceramics by $TiO_2$ addition

$TiO_2$ 첨가에 의한 MgO 세라믹스의 표현 수화 저항성 향상

The effect of $TiO_2$addition on the hydration reaction of MgO ceramics were studied after being heated at $1450^{\circ}C$. The pure MgO ceramics showed significant weight change after exposure to water due to the hydration reaction through the formation of $Mg(OH)_2$while $TiO_2$-added MgO ceramics did not. The $Mg_2TiO_4$phase were observed in the $TiO_2$-added MgO ceramics sintered at 145$0^{\circ}C$. Bulk density increased as the amount of $TiO_2$increased and the apparent porosity and water absorption decreased by $TiO_2$addition. The hydration resistance of MgO ceramics was found to be improved by $TiO_2$addition.

MgO를 기질로 한 세라믹스 시편에 $TiO_2$를 소량 첨가하고 $1450^{\circ}C$에서 열처리한 후 $TiO_2$를 첨가한 MgO 세라믹스의 수분에 대한 수화 반응에 미치는 영향을 조사하였다. $TiO_2$를 첨가하지 않은 MgO 세라믹스는 수분에 대한 수화반응에 의한 $Mg(OH)_2$의 생성으로 인한 질량변화가 관찰되었으나, $TiO_2$를 첨가함 MgO 세라믹스는 수분첩촉시간에 따른 질량변화가 관찰되지 않았다. $TiO_2$를 첨가한 MgO 세라믹스를 $1450^{\circ}C$에서 열처리했을 때, $Mg_2TiO_4$ 상이 관찰되었으며 특히 TiO$_2$를 첨가함에 따라 부피비중은 첨가량에 비례하며 증가한 반면에 가공율과 흡수율은 감소하는 경향을 나타내었다. 따라서 MgO 를 기질로 한 세라믹스에 $TiO_2$를 소량 첨가한 경우 표면에서 발생하는 수화 반응에 대하여 높은 저항성을 가짐을 확인하였다.