Synthesis of cobalt powder with polyol process

폴리올법을 이용한 미립 코발트 분말 합성

Fin metal particles of uniform shape, narrow size distribution and high purity are increasingly needed for specific uses in high tech industrial applications. Polyol process for the preparation of monodispersed cobalt powders in micron size is described. In this process in inorganic precursor is reduced in liquid polyol under controlled conditions. The reducing agent is the polyol itself and reaction parameters such as the traction temperature, reaction time, addition of protective agent and concentration of the precursor are varied for controling particles size, shape and agglomeration of the metal particles. An optimum synthesis condition was achieved at E.G/DiE/G volume ratio 1:4,Co$(OH)_{2}$polyol molar ratio 0.08~0.32 reaction temperature $210^{\circ}C$, PVP/Co$(OH)_{2}$ molar ratio 0.4.

균질한 형상, 좁은 입도분포 그리고 순도가 높은 미립 금속분말은 첨단산업분야에서 응용분야가 점차 확대되고 있다. 본 연구에서는 Polyol법을 이용한 마이크론 크기의 단분산 코발트 분말을 합성하였다 Polyol이 환원제 역할을 하였다. 반응온도, 반응시간, 분산제첨가 및 전구체의 농도 등을 변화시켜 코발트의 입자 크기, 형상 그리고 응집현상을 제어하고자 하였다. 최적의 합성조건은 E.G/DiE/G 부피비 1:4,$Co(OH)<_{2}$polyol 몰비 0.08~0.32 반응온도 $210^{\circ}C$, PVP/Co$(OH)_2$ 몰비 0.4이었다.