Formation of Hexagonal Ferrite $Co_2$Z(${Ba_3}{Co_2}{Fe_{24}}{O_{41}}$) Prepared by Coprecipitation-oxidation Method

공침산화법에 의한 육방정 페라이트 $Co_2$Z(${Ba_3}{Co_2}{Fe_{24}}{O_{41}}$)의 생성

Hexagonal ferrite $Co_2$Z(B $a_3$ $Co_2$F $e_{24}$ $O_{41}$ ) was prepared by various coprecipitation-oxidation methods. The formation of $Co_2$Z was studied in order to determine the optimal method. The $Co_2$Z composition hydroxides were prepared with the different oxidation and precipitation from the aqueous solution of $Ba^{2+}$, $Co^{2+}$ and F $e^{2+}$ chloride mixture. The coprecipitates were heat-treated at various temperatures, and their formation phases and microstructures were investigated from the analyses of DTA/TGA, powder XRD and SEM. The $Co_2$Z phase was observed in the case where the precursor will have the amorphous like oxyhydoxide($\delta$-FeOOH), and formed from $Ba_3$F $e_{32}$ $O_{51}$ , BaF $e_{12}$ $O_{19}$ (M-type) and $Ba_2$ $Co_2$F $e_{12}$ $O_{22}$ (Y-type). The $Co_2$Z was synthesized by the heat-treatment of the coprecipitate, which was prepared from the precipitation after oxidizing the chloride mixed solution, above 110$0^{\circ}C$.EX>.

육방정 페라이트 $Co_2$Z(B $a_3$ $Co_2$F $e_{24}$ $O_{41}$ )를 여러 공침-산화 방법으로 제조하여 생성과정을 연구하였으며, 적절한 제조 방법을 결정하였다. 산화 및 공침 순서를 다르게 하여 $Ba^{2+}$, $Co^{2+}$, F $e^{2+}$ 등의 염화물 혼합 수용액으로부터 $Co_2$Z 조성의 수산화물을 제조하였다. 그리고 열처리 온도에 따른 생성상의 변화를 열분석(DTA/TGA), 분말 X-선 회절분석, 주사전자현미경 등을 이용하여 관찰하였다. $Co_2$Z 상은 출발물질이 비정질에 가까운 산수산화철($\delta$-FeOOH)일 경우에만 관찰되었으며, $Ba_3$F $e_{32}$ $O_{51}$ , BaF $e_{12}$ $O_{19}$ (M형), $Ba_2$ $Co_2$F $e_{12}$ $O_{22}$ (Y형)로부터 생성되었다. 염화물 혼합 수용액을 산화시킨 다음 침전하여 합성한 공침물은 110$0^{\circ}C$부터 $Co_2$Z가 생성되었다.