Abstract
Microwave dielectric properties of Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_3$-Sr(Zn$_{1}$3/Nb$_{2}$3/) $O_3$(BZN-SZN) system were investigated as a function of sintering temperature and Zr $O_2$content. Density was increased and the temperature coefficient of resonant frequency (TCF, $\tau$$_{f}$) decreased with increasing sintering temperature. However dielectric constant (K) and Q$\times$f value did not change markedly with the sintering temperature. For the samples sintered at the same temperature, density, dielectric constant, and Q$\times$f value were increased and TCF was decreased with increasing Zr $O_2$concentration. Especially, the dielectric constant of the sample increased with x and exhibited the maximum value ($\varepsilon$$_{r}$=41) when x=0.6 at 1575$^{\circ}C$ sintered. TCF decreased with x and exhibited the minimum value ($\tau$$_{f}$=+0.8ppm/$^{\circ}C$) when x=1.0..0.
Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_3$-Sr(Zn$_{1}$3/Nb$_{2}$3/) $O_3$계에 대하여 소결 온도 변화와 Zr $O_2$첨가량에 따른 마이크로파 유전특성을 조사하였다. 동일 조성에서 소결 온도가 증가함에 따라 밀도가 향상되고 공진 주파수의 온도계수($ au$$_{f}$)는 감소하는 경향을 보였으나, 유전상수(K)와 품질계수(Q$\times$f)는 커다란 변화가 없었다. 또한 Zr $O_2$첨가량이 증가함에 따라 소결 시편의 밀도가 향상되었고 더불어 유전상수, 품질계수가 증가하는 경향을 보였으며, 공진 주파수의 온도계수가 감소하는 우수한 특성이 나타났다. 특히, 소결온도 1575$^{\circ}C$, 0.6 wt% Zr $O_2$를 첨가했을 때 유전상수가 최대($\varepsilon$$_{r}$=41)로 나타났으며, 공진 주파수의 온도계수는 1.0wt% Zr $O_2$를 첨가했을 때 최소($\tau$$_{f}$=+0.8ppm/$^{\circ}C$)로서 양호한 값을 얻을 수 있었다.었다.