Generally, polymer mortar made with unsaturated polyester(UP) resin has a high curing shrinkage. This is an inadequate as repair material and construction products that have been widely used for years recently. To overcome these problems, polymer researchers and engineers have used shrinkage-reducing additives, which are usually specific thermoplastic polymers. The objective of this study is to evaluate the effects of shrinkage-reducing additive on the curing shrinkage and strengths of UP mortar. UP mortars are prepared with expanded polystyrene(EPS) ratio in styrene monomer(SM), (EPS/PS, PS=EPS+SM), and the ratio of total polystyrene resin(PS) to UP resin, (PS/UP). And it is tested for viscosity of UP resin, slump-flow, working life, flexural and compressive strengths, and curing shrinkage tests. From the test results, viscosity of resin for UP mortar increases with increasing PS content. Curing shrinkage of UP mortar is considerably smaller than that of plain UP mortar, nevertheless, reduction in the strengths is not recognized according to adding PS resin. In this study, we can obtain the optimum mix proportions of UP mortar using PS resin which made of waste expanded polystyrene.
본 연구에서는 열경화성인 UP 수지에 열가소성 스티렌 수지를 혼합하여 사용함으로써 UP 수지의 경화기구 중 스티렌 수지가 수축보완 효과를 일으켜 UP 모르타르의 경화수축을 저감시킬 수 있다는 가능성을 확인하고자 실시하였으며 그에 따른 역학적 성질의 변화를 함께 검토하였다. 본 연구결과, 폐 스티로폴 용해액을 첨가한 불포화 폴리에스테르 수지의 점도는 EPS/PS비가 30% 미만일 경우는 PS/UP비가 증가함에 따라 감소하여 시공성 면에서 EPS/PS비가 30%이내에서 적절하였다. 또한 휨 및 압축강도는 EPS/PS비보다는 PS/UP비에 따른 영향이 크게 나타났으며 PS/UP비 30%이하에서 감소 정도가 작았으며, EPS/PS비와 PS/UP비가 증가함에 따라서 경화수축은 전체적으로 감소되는 경향을 보였다. 적절한 시공성과 휨 및 압축강도 특성 그리고 경화수축 시험의 종합적인 결과, EPS/PS비 30%, PS/UP비 30%일 때 최적의 배합 조건으로 나타났다. 이로서 폐 스티로폴을 UP 모르타르이 수축저감제로서 사용함에 있어 역학적 성질의 큰 변화 없이 경화수축을 제어할 수 있다는 결과를 얻어 실제현장에서의 사용성이 기대되며, 또한 본 연구에서 사용한 스티렌 수지는 폐 발포 폴리스티렌을 스티렌 모노머에 액화시킨 것으로서 폐기물로 발생되는 폐 스티로폴의 자원재활용의 측면에도 그 의미가 있다고 할 수 있다.