Abstract
The particulates reinforced metal matrix composites(PMMC) have a number of interesting mechanical properties. including high strength and good resistance to wear at high temperature and low thermal expansion. The equipment structure to obtain the homogeneous distribution in composites are proposed for the continuous pouring of reinforcement at the desired temperature. The particulates reinforced metal matrix composites(A357/SiCp) were fabricated by the process of the combined stirring method with the various fabrication process. The combined stirring method to niform distribution of particle is consisted of two stirring force both electro-magnetic stirring generated from induction heating and mechanical stirring with graphite stirrer. PMMC billets were fabricated with the volume fractions ranged from 0% to 20% and particle sizes ranged from 14${\mu}{\textrm}{m}$ to 25${\mu}{\textrm}{m}$. It is important to cont the size of primary $\alpha$-Al solid particles because it could become the cause of the particle pushing or capture phenomena from the fact that secondary dendrite arm spacing size depends on the cooling rate during the solidification in hypoeutectic Al-Si alloy. Therefore, the effect of primary $\alpha$-Al on the reinforcement distribution in matrix alloys has been investigated. The microstructure of PMMC fabracated with various volume fractions(0%, 10%, and 20%) and particle size were observed.
본 논문은 금속복합재료를 반용융상태로 재가열하여 Thixoforming을 하는데 필요한 소재를 제공하기 위한 장비 설계와 제조방법 등에 관한 내용을 소개하고 있다. 장비 설계에서 기지재내에 강화재가 균일하게 분산되도록 하기 위하여 강화재의 연속주입 방법과 강화재의 온도를 제어하는 방법을 소개하고 있다. 일정한 양의 강화재를 기지재료 내에 분산시키는 것은 균일 혼합을 위하여 필요한 기술이다. 또한 분산시 강화재의 수분제거를 위하여 강화재의 온도를 제어하면서 연속적으로 강제분산시키는 것은 균일분산을 위하여 필요하다. 기지재의 초정 $\alpha$의 크기가 강화재의 분산성에 크게 영향을 미치기 때문에 기지재의 초기 온도가 초정$\alpha$의 크기에 미치는 영향 등을 검토하여 복합재료 빌렛트의 제조조건에 이용하였다.