미소인공결함의 위치에 따른 마찰용접부의 피로특성

Fatigue Properties of Friction Weld According to the Location of Small Artificial Defect

In this study, the rotary bending fatigue test was carried out with two kinds of base metal, martensite stainless steel STR3 and austenite stainless steel STR35 and the dissimilar friction welded material with them. To compare the fatigue fifes according to the notch positions, the small circular defect was worked on the bonded line, 1.0mm and 0.5mm distance form the bonded line. The fatigue limits of the STR3 and STR35 base metal were 429.0MPa and 409.4MPa respectably. In comparison with fatigue life at the same notch positions, the STR35 specimens showed about 190% for base metal, 82% for 1.0mm distance notched specimens higher than that of the STR3. But the fatigue life of the 0.5mm distance notched STR35 specimen showed about 35% lower than that of the STR3 specimen. And the bonded line notched specimen was much lower fatigue life than the other specimens because of separation of the bonded line.