Temperature Effect on Tensile Strength of Filled Natural Rubber Vulcanizates

가황 천연고무의 인장강도에 미치는 온도의 영향

This study was related with the effect of elevated temperature on the tensile strength of edge-cut samples. There was a different tensile strength behavior of uncut samples and pre-cut samples under different test temperatures. Tensile strength of uncut sample decreases with increasing test temperature. When pro-cut size(C) is larger than critical cut size($C_{cr}$), tensile strength or pre-cut specimen at $80^{\circ}C$ is higher than that of pre-cut specimen at room temperature (RT). Test specimens under $80^{\circ}C$ condition exhibited more secondary cracks at the crack tip region compared to room temperature conditions. However, secondary cracks of pre-cut specimens are not clearly developed at $110^{\circ}C$. Differences in tensile strength induced by different test temperature seem to be responsible for the strain-induced crystallization and micro-cracking patterns.

Precut을 가지고 있는 고무 시편에서 서로 다른 온도에서 인장 강도의 영향을 조사하였다. 온도 조건에 따라 precut이 있는 시편과 precut이 없는 시편의 인장 강도는 서로 다른 거동을 보였다. $80^{\circ}C$에서는 임계 Precut 크기보다 더 큰 precut를 가지는 시편은 상온에서 시편보다 높은 인장 강도를 보였다. 상온에서 측정한 시편에 비하며 $80^{\circ}C$에서 측정한 시편은 잘 발달된 2차 균열들을 가지고 있는 반면, $110^{\circ}C$에서 측정한 시편의 경우 2차 균열들이 명확하게 발달하지 못하였다. 서로 다른 온도에서 인장강도의 차이는 인장시 발달된 결정화도와 균열 끝 부분에서 형성된 미세 균열 형상과 관계가 있는 것으로 보인다.