A Study on the Properties of Two-Component Type Polyurethane Resins Mixing Polyol and 4,4'-diphenyl Methane Diisocynate

폴리올(polyol)과 4,4'-디페닐메탄디이소시아네이트(MDI)를 혼합한 2액형 폴리우레탄 수지의 물성에 관한 연구

  • 이범철 ((주)화승 R&A 기술연구소) ;
  • 최상구 (호원대학교 공업화학과)
  • Published : 2001.12.31

Abstract

The MDI(4,4'-diphenyl methane diisocyanate) was mixed with PPG, PEG and trimethylolpropane(TMP) respectively to prepare polyurethane resin. The various physical properties were measured for the mixtures. The gel-time was shortened by adding of PEG and TMP The molecular weight made a greater influence on the gel-time than the number of functional groups. The NCO-OH reaction was more active and faster than the NCO-NCO reaction. The hardness was influenced by crosslinking-density and molecular structure. The NCO-OH reactions yielded the flexible films and the NCO-NCO reactions yielded the brittle films. The increase of crystallinity and shrinkage induced the low adhesion ratio but the adding of TMP induced the high adhesion ratio. The flame-retardancy was influenced by quantity and kinds of flame-retardant. IXOL B-251 was the most excellent among the flame-retardants employed in this study. TCCP was partially separated because of the lack of solubility.

PPG, PEG, trimethylolpropane(TMP) 등의 폴리올에 MDI(4,4'-diphenyl methane diisocyanate)를 각각 혼합하고 경화시켜 여러가지 물성을 측정하였다. 경화시간은 PEG와 TMP의 함량이 늘어날수록 짧게 나타났고 분자량의 효과보다는 관능기의 수에 더 큰 영향을 받았다. NCO-OH 반응은 NCO-NCO반응보다 활성적이고 빠르게 일어났다. 경도는 가교밀도와 분자구조의 영향을 받았으며 NCO-NCO 반응으로 생긴 도막은 취약하였고 NCO-OH간의 반응으로 생긴 도막은 유연하였다. 부착력은 결정화도와 수축율이 클수록 낮은 값을 나타내었으며 TMP 함량이 증량될수록 높은 값을 나타내었다. 난연성은 난연제의 종류와 함량에 영향을 받았으며 난연효과는 IXOL B-251이 가장 우수하였고 TCCP는 수지와의 상용성이 좋지 않아 부분적으로 분리되었다.

Keywords