Fracture Behavior of Silicon Nitride-silicon Carbide-boron Nitride Multi-layer Composites with Different Layer Thickness

  • Cho, Byoung-Uk (Department of Materials Science and Engineering, Pusan National University) ;
  • Park, Dong-Soo (Ceramic Materials Group, Korea Institute of Machinery and Materials) ;
  • Park, Hong-Chae (Department of Materials Science and Engineering, Pusan National University)
  • Published : 2002.07.01
Download PDF
⟨ Previous Next ⟩

Abstract

Multi-layer composites consisting of silicon nitride, silicon nitride-silicon carbide and boron nitride-alumina layers were prepared fly stacking the corresponding ceramic tapes. The composites demonstrated self-diagnostic capability and non-catastrophic failure behavior. The composites consisting of many thin layers exhibited high strength and stepwise increase of the electrical resistance during the flexure test. The strength of the composite with too thick silicon nitride layers was low and the electrical resistance was abruptly increased to the detection limit of the digital multi-meter during the test. An extensive crack branching was observed in the weak (BN + Al$_2$O$_3$)layer.

Keywords

References

  1. Nature v.347 A Simple Way to Make Tough Ceramics W. J. Klegg;K. Kendall;N. McN. Alford;T. W. Button;J. D. Birchall https://doi.org/10.1038/347455a0
  2. Acta Metall. Mater. v.41 no.3 Fracture Behavior of Ceramic laminates in Bending-Ⅱ. Comparison of Model Predictions with Experimental Data A. J. Philipps;W. J. Clegg;T. W. Clyne https://doi.org/10.1016/0956-7151(93)90015-K
  3. J. Am. Ceram. Soc. v.79 no.9 Facture Behvior of Multilayer Silicon Nitride/Boron Nitride Ceramics H. Liu;S. M. Hsu https://doi.org/10.1111/j.1151-2916.1996.tb08996.x
  4. J. Am. Ceram. Soc. v.80 no.7 Debonding in Multilayered Composites of Zirconia and LaPO₄ D. B. Marshall;P. E. D. Morgan;R. M. Housley https://doi.org/10.1111/j.1151-2916.1997.tb03038.x
  5. J. Am. Ceram. Soc. v.76 no.9 Fibrous Monolith Ceramics:Ⅱ, Flexural Strength and Fracture Behavior of the Silicon Carbide/Graphite System S. Baskaran;J. W. Halloran https://doi.org/10.1111/j.1151-2916.1993.tb07757.x
  6. Kor. J. Ceram v.6 no.2 Damage Detection in Fiber Reinforced Composites Containing Electrically Conductive S-G. Shin;H. Matsubara
  7. J. Mater. Sci. Lett.(in print) Variation of Electrical Resistance during Fracture of Silicon Nitride-silicon Carbide Whisker-Boron Nitride Laminate Composite D-S. Park;H-D. Kim;B-D. Han;T-W. Roh;C. Park;B-W. Cho;H-C.Park
  8. J. Am. Ceram. Soc. v.73 no.8 Electrical Resistivity of Composites D. S. McLachian;M. Blaszkiewicz;R. E. Newham https://doi.org/10.1111/j.1151-2916.1990.tb07576.x
  9. J. Am. Ceram. Soc. v.81 no.10 Mechanical Properties of Si₃N₄-SiC Three-layer Composite Materials B-J. Choi;Y-H. Koh;H-E. Kim https://doi.org/10.1111/j.1151-2916.1998.tb02685.x
  10. Int. J. Fraacture v.44 Behavior of Indentation Cracks near Free Surface and Interfaces T. J. Lardner;J. E. Ritter;M. L. Shiao;M. R. Lin https://doi.org/10.1007/BF00047064