Abstract
The purpose of this research was to develop a rapid setting cement latex modified concrete (RSLMC) for bridge deck repairing and overlaying. The main experimental variables were latex contents, antifoamer contents and water-cement ratioes. The workability, strength development and permeability were measured as responses. The results showed that latex content increased the slump and reduced the unit water required for same workability. The air contents were measured as 8.0∼9.0％ and 2.0∼3.0％ without antifoamer and with 1.6∼3.2％ of antifoamer, respectively. This resulted in the increment of compressive strength development by 10∼20 ％. The flexural strength of RSLMC increased greatly as the latex content increased, but not in compressive strength. The compressive strength and flexural strength developed enough for opening the overlayed RSLMC to the traffic after 3 hours of RSLMC placement. The permeability of RSLMC was evaluated as negligible due to its very low charge passed. Thus, RSLMC could be used at repairing or overlaying the concrete bridge deck at fast-track job sites.
본 연구에서는 기존 교량의 신속한 유지보수를 위한 교면포장 덧씌우기용 라텍스개질 초속경 콘크리트를 개발하고자 하였다. 실험변수로는 국내 생산 초속경 시멘트를 이용하여 혼화제 인자로 라텍스 및 소포제 혼입률 변화를 선정하여 작업성, 강도발현 및 투수 특성을 고찰하고자 한다. 실험결과 동일 물-시멘트비 조건에서의 라텍스 혼입은 콘크리트의 슬럼프를 증대시켜 작업성을 유지하기 위한 단위수량을 감소시키는 것으로 나타났다. 소포제를 혼입하지 않을 때는 공기량이 8~9%로 나타났으나, 소포제를 1.6~3.2% 혼입함으로써 공기량이 2.0~3.8%로 감소되었으며, 이로 인해 압축강도가 10~20%정도 증진하였다. 라텍스의 양이 증가함에 따라 콘크리트의 휨강도는 증진되나, 압축강도는 다소 저하되었다. 그러나, 소포제의 혼입으로 타설 후 3시간 만에 교통개방을 위한 압축강도와 휨강도를 얻을 수 있었다. 라텍스를 일정량 이상 첨가할 경우 콘크리트를 불투수성의 재료로 평가할 수 있을 정도의 낮은 통과전하량을 나타내었다. 따라서 라텍스 개질 초속경 콘크리트는 구조물, 교량 포장의 덧씌우기 또는 보수재료로서 사용되어 질 수 있을 것으로 사료된다.