Abstract
Recently, the failure case of the bridge deck slabs have been increasing in Korea and it was observed that the failure modes of most deck slabs collapsed were not caused by flexural moment but by local punching shear. The main reason of the failures was the punching shear failure of deck slabs under heavy truck traffics. This paper presents test results obtained from punching shear tests performed on prestressed precast deck specimens. Cracking patterns, failure modes, deflections, and stresses are included as well as discussion of the punching shear strength observed during punching shear tests. Static lest specimens had punching shear failures at loads much higher than predicted by the current codes. Tests results indicate that current code provisions appear to be conservative.
최근들어, 국내에서 공용중인 교량바닥판의 파손사례가 증가되고 있으며, 파손된 바닥판의 주요 파괴모드는 반복되는 중트럭 하중에 의한 국부적인 펀칭전단이 주원인이 되고 있다. 본 연구에서는 교축방향으로 프리스트레스가 도입된 프리캐스트 콘크리트 교량바닥판에 대해서 펀칭전단 파괴실험을 수행하여 펀칭전단 실험중에 얻어진 균열양상, 파괴모드, 처짐 및 응력 특성, 펀칭전단강도 등을 검토하였다. 정적 펀칭전단 실험결과 교량바닥판의 펀칭전단 파괴는 현행 시방서의 예측식에값 보다 더 큰 하중 수줄에서 발생되어 현행 시방서에서 규정하는 펀칭전단 강도는 안전측의 결과를 보이는 것으로 판단된다.