Abstract
When forming the ceramic body with plastic mass, it is needed that a quantitative testing method for plasticity, not only to evaluate the plasticity of a body, but also to control it within limits. Although many testing instruments were introduced, but no handy testing instrument for the plasticity quantitatively has been developed. In this study, modified vicat needle was designed to handily evaluate the plasicity of extruding bodies for honeycomb. The plasticity of three plastic masses was tested with this equipment. Columned needle with 2 mm diameter was adopted to measure the resistance for deformation and spherical needle with 9.5 mm diameter was adopted to measure the amount of deformation before cracking. The plasticity of three tested bodies were clearly distinguished quantitatively each other and the testing results were helpful to evaluated the workability of theses bodies. Probably, it is possible to evaluate the plasticity of various ceramic bodies with this apparatus, if suitable diameters of columns and spheres are selected.
가소성 소지를 이용하여 세라믹을 성형하는 경우에 소지의 가소성 평가뿐만 아니라 이를 범위 내에서 제어하기 위하여도 가소성을 정량적으로 시험할 필요가 있다. 비록 많은 가소성 측정 장치들이 소개되기는 하였으나, 간편하게 정량적으로 측정할 수 있는 장치는 아직 없다. 본 연구에서는 바이카 침을 변형하여 허니컴 압출성형용 소지의 가소성을 간편하게 정량적으로 비교할 수 있는 장치를 만들었다. 이 장치를 사용하여 3가지 소지의 가소성을 조사하였다. 변형에 대한 저항의 측정에는 직경 2 mm 원주형 침을 사용하였고, 균열이 일어나기 전까지의 변형 량의 측정에는 직경 9.5 mm 구형의 침을 사용하였다. 측정결과 이 소지들의 가소성을 정량적으로 구분할 수 있었으며, 작업성을 평가하는데 유용하였다. 만약 적당한 직경의 원주형 및 구형의 침을 선택한다면 이 장치로 다양한 세라믹 소지의 가소성을 평가할 수 있을 것으로 보인다.