Effect of Glass Composition on the Properties of Glass-infiltrated Alumina(I) : Effect of Al2O3

유리가 침투된 알루미나 복합체의 물성에 미치는 유리조성의 영향(I): Al2O3의 영향

  • 이재희 (인하대학교 세라믹공학과) ;
  • 김철영 (인하대학교 세라믹공학과)
  • Published : 2003.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Glass-infiltrated alumina, which can be used as an all-ceramic dental crown, was prepared. The glasses in the system of SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$with various amount of $Al_2$O$_3$infiltrated into a porous sintered alumina. The effect of $Al_2$O$_3$on the infiltration characteristics and its mechanical strength were studied. The corrosion of the sintered alumina by infiltrated glasses was prevented by increasing the amount of $Al_2$O$_3$in the glass batches, this increased the bending strength of the glass infiltrated alumina composite. The crack like voids in the sintered alumina was a cause of the deteriorating the mechanical strength of the composite, and this can be eliminated by sintering the alumina at 130$0^{\circ}C$. Glass infiltration under the vacuum atmosphere enhanced the hording strength of the composite up to 453$\pm$31 MPa.

완전 세라믹 치관 재료로 응용할 수 있는 유리가 침투한 알루미나 복합체를 제조하였다. SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$계 유리에서 $Al_2$O$_3$의 함량을 변화시키며 다양한 조성의 유리를 만들고 이들 유리를 저온 소결한 다공성 알루미나에 침투시켰다. 그리고 이때 A1$_2$O$_3$의 함량변화가 유리의 침투 특성과 얻어진 복합체의 강도에 미치는 영향에 대하여 연구하였다. 유리 조성에서 A1$_2$O$_3$의 양을 증가시킬수록 알루미나 소결체의 부식 현상이 현저히 줄었으며 이에 따라 복합체의 강도가 증가하였다. 알루미나 소견체에는 거대기공이 존재하고 있어 복합체의 강도 저하에 영향을 미쳤는데 알루미나의 소결 온도를 130$0^{\circ}C$까지 증가시켜 이를 감소시켰다. 진공 분위기에서 알루미나 소결체에 유리를 침투시켰을 때 최고 453$\pm$31 MPa의 굽힘 강도 값을 얻을 수 있었다.

Keywords

References

  1. Ceramic and Glasses v.4 Dental Application;in Engineered Materials Handbook A.E.Clark;K.J.Anusavice
  2. J. Mater. Res. v.11 no.4 Microstructure of a High Strength Alumina Glass Composite H.Hornbergar;P.M.Marquis https://doi.org/10.1557/JMR.1996.0104
  3. J. Am. Ceram. Soc. v.76 no.10 Melt-infiltration Processing and Fracture Toughness of Alumina-glass Dental Composites W.D.Wolf;L.F.Francias;C.P.Lin;W.H.Douglas https://doi.org/10.1111/j.1151-2916.1993.tb04004.x
  4. Dent. Clin. North Am. v.29 no.4 Development of Dental Ceramics-An Historical Approach D.W.Jones
  5. Br. Dent. J. v.119 no.6 The Reinforcement of Dental Porcelain with Ceramic Oxides J.W.McLean;T.H.Hughes
  6. J. Ceram. Soc. Jpn., Inter. v.97 Preparation of Glass-ceramics Containing Crystalline Apatite and Magnesium Titanate for Dental Crown T.Kokubo;S.Sakka;M.Sako;S.Ikejiri
  7. J. Am. Ceram. Soc. v.67 no.7 Calcium Phosphate Glass-ceramics Crown Prepared by Low-wax Technique S.Kimura;A.Watanabe
  8. J. Euro. Ceram. Soc. v.18 The Infiltration of Cobalt Silicides into Silicon Carbide Preforms Y.Pan;J.L.Baptista https://doi.org/10.1016/S0955-2219(97)00105-2
  9. Am. Ceram. Soc. Bull. v.76 no.4 Fabrication of Al₂O₃Al Composites by Reaction Melt Infiltration W.P.Tai;T.Watari;T.Torikari
  10. Quintessence Int. v.23 no.1 Slip Casting Alumina Ceramic for Crown and Bridge Restoration L.Probster;J.Diehl
  11. J. Kor. Ceram. Soc. v.38 no.9 Glass-alumina Composites Prepared by Melt-infiltration: I. Effect of Alumina Particle Size D.Y.Lee;J.W.Jang;D.J.Kim;I.S.Park;J.K.Lee;M.H.Lee;B.Y.Kim
  12. J. Kor. Ceram. Soc. v.39 no.2 Glass Alumina Composites Prepared by Meltinfiltration: Ⅱ. Kinetic Studies D.Y.Lee;J.W.Jang;M.H.Lee;J.K.Lee;D.J.Kim;I.S.Park https://doi.org/10.4191/KCERS.2002.39.2.145
  13. Kor. Stand. Soc. Testing Method for Flexural Strength (Modulus of Rupture) of High Performance Ceramics Korean Industrial Standard KSL 1591
  14. J. Am. Ceram. Soc. v.66 no.6 Processing-related Fracture Origins: Ⅲ, Differential Sintering of ZrO₂Agglomerates in Al₂O₃/ZrO₂Composite F.F.Lange;B.I.Davis https://doi.org/10.1111/j.1151-2916.1983.tb10070.x
  15. Glass Engineering B.H.Kim
  16. Chemical Approach to Glass M.B.Volf
  17. J. Am. Ceram. Soc. v.79 no.9 Mechanical Properties Failure Anlaysis Glass-alumina Dental Composites W.D.Wolf;K.J.Vaidya;L.F.Francis https://doi.org/10.1111/j.1151-2916.1996.tb07994.x
  18. J. Am. Ceram. Soc. v.82 no.10 Peamiability and Infiltration of Partially Sintered Ceramics S.J.Glass;D.J.Green https://doi.org/10.1111/j.1151-2916.1999.tb02151.x