Abstract
The changes of microstructure and hardness of TLP bonds of directionally solidified Ni base superalloy, GTD-111, with variation of homogenizing and aging treatment were investigated. The specimens were bonded at 1403K for 7.2ks using different insert metals such as MBF-50, MBF-80 and MBF-90 and they were homogenized at 1393K with various holding time. At center of bonded interlayer homogenized for hold time 30h, the contents of aluminum and titanium were approximately 90% and 95% of base metal, respectively. In this study, aging was performed at three different kinds : one step aging ; 1113K $\times$ 16h, two step aging ; 1113K $\times$ 10h ⇒ 1103K $\times$ 10h, three step aging ; 1113K $\times$ 10h ⇒ 1103K $\times$ 8h ⇒ 922K $\times$ 24h. ${\gamma}$' volume fraction and hardness of joints were high in the sequence of one step, two step and three step aging, whereas ${\gamma}$' volume fraction and hardness of joints obtained by three step aging treatment were higher than those of raw material. Tensile properties of joints bonded with MBF-80 and MBF-90, homogenized at 1393K for 30h and then three step aged became excellent than those of raw material, however, joint bonded with MBF-50 was poor.