Characteristics of Nickel Aluminate Ceramics Synthesized by Organic (PVA)-Inorganic Solution Technique

PVA 폴리머를 이용한 니켈 알루미네이트 분말의 합성 및 특성연구

  • 이상진 (국립목포대학교 신소재공학전공) ;
  • 김주원 (국립목포대학교 신소재공학전공)
  • Published : 2003.07.01
Download PDF
⟨ Previous Next ⟩

Abstract

Soft-solution route employing PVA(Polyvinyl Alcohol) as a polymeric carrier in a mixed metal cation solution was used for synthesis of single-phase nickel aluminate (NiA1$_2$O$_4$) powders. The PVA ensured the homogeneous distribution of metal ions in the solution and it resulted in the decrease of crystallization temperature. The synthesized powders prepared by PVA addition were soft and ball-milled easily. The ball-milled powders of about 300 nm in size were fully densified to density of 4.35 g/㎤ at 1600$^{\circ}C$ for 1 h. The Vickers hardness, flexural strength, fracture toughness and thermal expansion coefficient of the sintered nickel aluminate were 14.2 ㎬, 304 ㎫, 4.8 ㎫$.$m$\^$1/2/ and 9.8${\times}$10$\^$-6//$^{\circ}C$, respectively.

고순도의 세라믹분말을 합성할 수 있는 용액 화학적 합성방법의 하나로서, 폴리머를 이용한 분말합성방법이 개발되었다. 본 연구에서는 PVA(Polyvinyl Alcohol)을 이용하여 니켈 알루미네이트(NiAl$_2$O$_4$) 분말을 합성하였다. PVA 첨가에 의하여 용액내의 금속 양이온들의 분산을 극대화하며, 순수한 니켈 알루미네이트를 얻기 위한 결정화 온도를 낮출 수 있었다. PVA 폴리머를 이용함으로써 분쇄가 용이한 부드러운 팽창성 분말을 얻을 수 있었으며, 볼 밀링에 의하여 약 300 nm의 크기를 보이는 좁은 입도의 미세한 분말이 얻어졌다 1$600^{\circ}C$, 1시간 소결에 의하여 4.35 g/㎤의 밀도를 보이는 치밀한 니켈 알루미네이트를 얻을 수 있었으며, 측정된 경도, 곡강도, 파괴인성 및 열팽창계수 값은 각각 14.2 ㎬, 304 ㎫, 4.8 ㎫.m$^{1}$2/과 9.8$\times$$10^{-6}$/$^{\circ}C$를 보였다.

Keywords

References

  1. J. Am. Ceram. Soc. v.72 no.5 Structural and Thermodynamic Variation in Nickel Aluminate Spinel K.Mocala;A.Navrotsky https://doi.org/10.1111/j.1151-2916.1989.tb06225.x
  2. Phase Diagrams for Ceramists v.2 R.S.Roth;J.R.Dennis;H.F.McMurdie
  3. Mater. Sci. & Eng. v.B90 Preparation of Nanosized Nickel Alumiate Spinel by a Sono-chemical Method P.Jeevanandam;Y.Koltypin;A.Gedanken
  4. Colloids and Surfaces v.A180 High Surface Area Nickel Aluminate Spinel Prepared by a Sol-gel Method C.O.Arean;M.P.Mentruit;A.J.Looped;J.B.Parra
  5. J. Mater. Chem v.9 Microemulsin Mediated Sol-gel Synthesis of Nano-scaled $MAl_{2}O_{4}$ (M=Co, Ni, Cu) Spinel from Single-source Heterobimetallic Alkoxide Precursors F.Meyer;R.Hempelmann;S.Mathur;M.Veith https://doi.org/10.1039/a900014c
  6. J. Am. Ceram. Soc. v.81 no.10 Crystallization and Densification of Nano-size Amorphous Cordierite Powder Prepared by a PVA Solution-polymerization Route S.J.Lee;W.M.Kriven https://doi.org/10.1111/j.1151-2916.1998.tb02667.x
  7. Ceram. Eng. and Sci. Proc. v.19 no.4 Preparation of Ceramic Powders by a Sloution-polymerization Route Employing PVA Solution S.J.Lee;W.M.Kriven https://doi.org/10.1002/9780470294499.ch55
  8. J. Am. Ceram. Soc. v.82 no.8 Preparation of Portland Cement Components by Poly(vinyl alcohol) Solution Polymerization S.J.Lee;E.A.Benson;W.M.Kriven https://doi.org/10.1111/j.1151-2916.1999.tb02039.x
  9. J. Am. Ceram. Soc. v.82 no.3 Polymerized Organic-inorganic Synthesis of Mixed Oxides M.A.Gulgun;M.H.Nguyen;W.M.Kriven https://doi.org/10.1111/j.1151-2916.1999.tb01800.x
  10. J. Mater. Res. v.14 no.8 Synthesis of Oxide Powders via a Polymeric Steric Entrapment Precursor Route M.H.Nguyen;S.J.Lee;W.M.Kriven https://doi.org/10.1557/JMR.1999.0462
  11. J. Kor. Ceram. Soc. v.39 no.4 Fabrication of Nano-sized Titanate Powder via a Polymeric Steric Entrapment Route and Plan-etary Milling Process S.J.Lee;C.H.Lee https://doi.org/10.4191/KCERS.2002.39.4.336
  12. U.S. Pat., No., 3 330 697, July 11, 1967 Method of Preparing Lead and Alkaline-earth Titanates and Niobates and Coating Method Using the Same to Form a Capacitor M.Pechini
  13. J. Am. Ceram. Soc. v.75 no.12 Mixed-cation Oxide Powders via Resin Intermediates Derived from a Water-soluble Polymer L.W.Tai;H.U.Anderson;P.A.Lessing https://doi.org/10.1111/j.1151-2916.1992.tb04458.x
  14. J. Am. Ceram. Soc. v.39 no.6 Low Temperature Synthesis of BaCeO₃ Nano Powders by the Citrate Process D.W.Lee;J.H.Won;K.Joo;C.Y.Kim;K.B.Shim https://doi.org/10.4191/KCERS.2002.39.6.604
  15. J. Ceram. Proc. Res. v.3 no.3 Characteristics and Densification Behavior of Anorthite Powder Synthesized by a Solution Process Employing a Polymer Carrier S.J.Lee;K.S.Kim
  16. M.S. Thesis, University of Illinois at Urbana-champaign, Urbana A New Polymer Route to the Synthesis of Mixed Oxide Ceramics M.H.Nguyen
  17. J. Mater. Sci. v.14 no.7 Powder Synthesis of Barium Titanate and Barium Orthotitanate via an Ethylene Glycol Complexation Polymerization Route S.J.Lee;M.D.BiegalskiW.M.Kriven

Cited by

  1. Fabrication of Calcium Phosphate Glass Using Eggshell and its Crystallization Behavior vol.54, pp.5, 2017, https://doi.org/10.4191/kcers.2017.54.5.08