Abstract
Cement paste, mortar or concrete specimens, substituting the content of Portland cement with fly ash up to 50 wt%, were prepared to investigate the effect of fly ash on the temperature, free lime content and strength etc. of mortar/concrete. Being compared with the concrete made of ordinary Portland cement, temperature increment of the concrete containing 50 wt% fly ash reduced, according to appropriate conversion formulae, to about 45％ at the 7 days curing time: the temperature increment of the former amounted to 33.4$^{\circ}C$, while that of the latter only to 18.7$^{\circ}C$. On the other hand, it is better to control the content of fly ash in the cement that is used for reinforced concrete not to exceed 30 wt％. In this study, more than 28 days curing time is necessary in order that the strength of concrete made of fly ash cement will be higher than that of pure Portland cement. In addition, 28-days concrete strength higher than 360 kg/$\textrm{cm}^2$ could be easily achieved even with 50 wt% fly ash cement.
포틀랜드 시멘트 양(중량)을 플라이 애쉬로 50 wt%까지 치환한 페이스트, 모르터 내지 콘크리트 시편을 만들어 플라이 애쉬가 모르터/콘크리트의 온도, 자유석회량 및 강도 등에 미치는 영향을 조사하였다. 페이스트의 수화열을 측정하여 환산식에 따라 일반 포틀랜드 시멘트 콘크리트의 경우와 비교할 때, 플라이 애쉬를 50 wt% 함유한 콘크리트의 양생 7일 온도(상승)는 약 45% 저하되었다. 전자의 경우 온도 상승은 33.4$^{\circ}C$이며 후자의 경우는 18.7$^{\circ}C$였다. 한편 철근 콘크리트의 제조에 사용되는 시멘트의 플라이 애쉬 함유량은 철근부식의 방지를 위하여 30 wt%를 초과하지 않는 게 바람직하다. 플라이 애쉬를 혼합한 콘크리트의 강도가 순수 포틀랜드 시멘트 콘크리트의 강도보다 양호하기 위해서는 양생기간이 28일 이상 되어야 한다. 그리고 플라이 애쉬 50 wt%를 함유한 시멘트를 가지고도 360 kg/$\textrm{cm}^2$ 이상의 28일 강도를 얻을 수 있었다.