Abstract
Microstructural and electromagnetic properties of YIG ferrites, (Y, Ca)-(Fe, V, In, Al)-O for Isolator/Circulator were investigated with the sintering temperature. YIG ferrites of $Y_{2.1}Ca_{0.9}Fe_{4.4}V_{0.5}In_{0.05}Al_{0.05}O_{12}$ were fabricated by sintering at $1300^{\circ}C$, $1330^{\circ}C$, $1350^{\circ}C$, $1370^{\circ}C$. Crystallographic and microstructural properties were measured using XRD and SEM. Saturation magnetization$(4{\pi}M_s)$ were measured using VSM, and FMR(Ferromagnetic Resonance) experiment was conducted to measure ferromagnetic resonance line width$({\Delta}H)$. Microwave characteristics of YIG ferrites were measured using a Network Analyzer. The YIG ferrite of $Y_{2.1}Ca_{0.9}Fe_{4.4}V_{0.5}In_{0.05}Al_{0.05}O_{12}$, sintered at $1350^{\circ}C$, showed higher density, saturation magnetization and lower ferromagnetic resonance line width than those sintered at any other temperature.
소결온도에 따른 아이솔레이터/서클레이터용 (Y, Ca)-(Fe, V, In, Al)-O 계 YIG 페라이트의 미세구조와 전자기적 특성을 고찰하였다. $Y_{2.1}Ca_{0.9}Fe_{4.4}V_{0.5}In_{0.05}Al_{0.05}O_{12}$ 조성의 시편들을 일반적인 세라믹 제조 공정에 따라 $1300^{\circ}C$, $1330^{\circ}C$, $1350^{\circ}C$, $1370^{\circ}C$에서 각각 소결하였다. 소결체는 XRD를 이용하여 상분석을 실시하였고, SEM을 이용하여 미세구조를 관찰하였다. VSM을 이용하여 포화자화값$(4{\pi}M_s)$을 측정하였으며, FMR(Ferromagnetic Resonance)실험으로 자기공명반치폭$({\Delta}H)$을 측정하였다. YIG 페라이트의 마이크로파 특성은 Network Analyzer를 이용하여 측정하였다. $Y_{2.1}Ca_{0.9}Fe_{4.4}V_{0.5}In_{0.05}Al_{0.05}O_{12}$ 조성의 YIG 페라이트는 $1350^{\circ}C$에서 소결시 가장 높은 밀도값과 포화 자화$(4{\pi}M_s)$ 값을 나타내었고, 가장 낮은 자기 공명 반치폭$({\Delta}H)$ 값을 나타내었다.