Composites are widely used for aircraft, satellite and other structures due to its good mechanical and thermal characteristics such as low coefficient of thermal expansion(CTE), heat-resistance, high specific stiffness and specific strength. In order to use composites under condition of high temperature, however, material properties of composites at high temperatures must be measured and verified. In this paper, material properties of T700/Epoxy were measured through tension tests of composite specimens with an embedded FBG sensor in the thermal chamber at the temperatures of RT, $100^{\circ}$, $200^{\circ}$, $300^{\circ}$, $300^{\circ}$. Through the pre-test of an embedded optical fiber, we confirmed the embedding effects of an optical fiber on material properties of the composites. Two kinds of specimens of which stacking sequences are [0/｛0｝/0]$_{T}$. and [$90_2$/｛0｝/$90_2$]. were fabricated. From the experimental results, material property changes of composites were successfully shown according to temperatures and we confirmed that fiber Bragg grating sensor is very appropriate to strain measurement of composites under high temperature.
복합재료는 비강성, 비강도가 높고 열팽창 계수가 낮으며 우수한 내열 특성 등 기계적, 열적 특성이 좋아 항공기, 인공위성을 비롯하여 여러 다른 구조물에 폭넓게 사용되고 있다. 하지만, 복합재료를 고온 환경에 사용하기 위해서는 고온 환경에서의 물성에 대한 검증이 필요하다. 본 연구에서는 FBG 센서가 삽입된 T700/Epoxy 복합재료 시편에 대해 온도에 따른 물성을 측정하였다 실험은 열챔버 내에서 수행하였고 온도 범위는 상온, $100^{\circ}$, $200^{\circ}$, $300^{\circ}$, $300^{\circ}$이다. 삽입된 광섬유의 예비 시험을 통해, 광섬유 센서의 삽입이 물성값에 미치는 영향을 확인하였다. 시험에는 [0/{0}/0]$_{T}$, [$90_2$/{0}/$90_2$] 와 같은 적층각을 갖는 두 종류의 시편을 사용하였다. 실험 결과로부터 온도에 따른 복합재료의 물성 변화를 성공적으로 측정하였으며 FBG 센서가 고온 환경의 변형률 측정 센서로 매우 적합함을 확인하였다.