Abstract
Reinforced concrete structures under sever conditions such as marine structures, bridges and structures constructed with aggregates(dredged from sea), can be deteriorated from corrosion of the reinforcing bars. The purpose of this study is to evaluate the anti-corrosive performance of coated steel using polymer cement slurry. Polymer cement slurry with various polymer dispersions and corrosion inhibiting agent were coated to the surface of bars, and tested for accelerated corrosion tests. Tests include immersion in NaCl 10% solution, chloride ion spray, autoclave cure, autoclave cure after carbonation, penetration of NaCl 10 % solution, carbonation after penetration of NaCl 10% solution. Test results, show that the anti-corrosive performace is considerably improved by using polymer cement slurry at surface of steel. And this trend is marked by adding of corrosion inhibiting agent. This difference of the anti-corrosive properties is hardly recognized according to types of polymer dispersions. The coated steel using polymer cement slurry will be improved to a great extent compared to those of plain steel when increasing content of chloride ion in cement concrete.
최근 강모래의 고갈로 인하여 해사의 사용이 증대되고 있는 실정에 있다. 그러나 해사는 철저하게 제염처리 하여 사용하지 않으면 철근 콘크리트 구조물의 철근에 막대한 영향을 미칠 수 있다. 본 연구에서는 제염처리하지 않은 해사를 시멘트 콘크리트에 직접 사용하여도 철근의 부식을 억제할 수 있는 방청재료를 개발하기 위한 연구의 일환으로서, 기존의 에폭시 철근과 비교하여 경제적이고 방식 성능면에서 우수한 재료로서 폴리머 시멘트 슬러리를 이용하고자 하였다. 각종 폴리머를 사용하고 여러 가지 부식촉진 실험을 통하여 도장하지 않은 철근과 도장한 철근과의 성능을 비교평가하였다. 연구결과, 폴리머 시멘트 슬러리로 도장한 철근은 도장하지 않은 철근에 비해 염화나트륨 수용액에 대한 침지 및 분무시험과 시멘트 콘크리트 속에서의 부식에 관한 실험에 있어서도 매우 우수한 방식성능을 발휘하였다. 다양한 부식촉진 실험결과, 철근의 부식은 염분, 중성화 및 촉진양생에 의해 크게 영향을 받으며, 복합적인 인자가 작용될 때, 더욱더 심한 부식이 발생하였다. 이러한 부식을 폴리머 시멘트 슬러리에 의한 도장으로 억제할 수 있는데, 폴리머 시멘트 슬러리의 매트릭스에 존재하는 폴리머 필림의 연속된 막에 의해 염화물 이온의 침투가 차단되었기 때문이며, 폴리머 시멘트 슬러리의 완벽한 방식효과는 도장두께로 조절할 수 있을 것이다.