Abstract
The effects of polymer-cement ratio, antifoamer content and shrinkage-reducing agent content on the air content, setting time, drying shrinkage and strength of polymer-modified mortars using redispersible polymer powder are examined. As a result, the air content of the polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio and antifoamer content. Regardless of the antifoamer content, the setting time of the polymer-modified mortars using redispersible polymer powder tend to delayed with increasing polymer-cement ratio. Irrespective of the antifoamer content, the drying shrinkage of the polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio and shrinkage-reducing agent content. Regardless of the antifoamer content, the flexural and tensile strengths of the ultrarapid-hardening polymer-modified mortars using redispersible polymer powder tend to increase with increasing polymer-cement ratio, and tend to decrease with increasing shrinkage-reducing agent content. However, the compressive strength of the ultrarapid-hardening polymer-modified mortars using redispersible polymer powder decrease with increasing polymer-cement ratio and shrinkage-reducing agent content.
본 연구에서는 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 공기량, 응결시간, 건조수축 및 강도특성에 미치는 분말소포제 첨가율 및 분말 수축저감제 첨가량의 영향에 대하여 검토하였다. 그 결과, 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 공기량은 분말소포제 첨가율 및 폴리머-시멘트비의 증가에 따라 감소하는 경향을 보였다. 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 응결시간은 분말소포제 첨가율에 관계없이 폴리머-시멘트비의 증가에 따라 늦어지는 경향을 보였다. 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 건조수축은 분말소포제 첨가율에 관계없이 폴리머-시멘트비 및 분말 수축저감제 첨가율의 증가에 따라 감소하는 경향을 보였다.또한 분말소포제 첨가율 및 분말수축저감제 첨가율에 관계없이 재유화형 분말수지를 혼입한 초속경 폴리머 시멘트 모르타르의 휨 및 인장강도는 폴리머-시멘트비의 증가에 따라 증가하는 경향을 보였으나, 압축강도는 감소하는 경향을 보였다.