Intermetallic Compounds Growth in the Interface between Sn-based Solders and Pt During Aging

시효처리에 따른 Cu를 포함하는 Sn계 무연솔더와 백금층 사이의 금속간화합물 성장

Interfacial reaction of Pb-free $Sn0.7wt{\%}Cu$ and $Sn3.8wt{\%}Ag0.7wt{\%}Cu$ solders and Pt during aging has been investigated. After the $Sn3.8wt{\%}Ag0.7wt{\%}Cu/Pt$ specimens were reflowed at $250^{\circ}C$ for 30s and the $Sn0.7wt{\%}Cu/Pt$ specimens were reflowed at $260^{\circ}C$, the specimens were aged at $125^{\circ}C,\;150^{\circ}C$ and $170^{\circ}C$ for 25-121 hours. The intermetallic thitkness and morphology change during aging were characterized using SEM, EDS and XRD. $PtSn_4$ and $PtSn_2$ were observed in the solder/pt interface and the intermetallic formation was governed by diffusion. The activation energy of intermetallic formation was 145.3 kJ/mol for$Sn3.8wt{\%}Ag0.7wt{\%}Cu/Pt$ specimens for $Sn0.7wt{\%}Cu/Pt$ specimens from the measurement of the intermetallic thickness with aging temperature and time.

무연솔더 $Sn0.7wt{\%}Cu,\;Sn3.8wt{\%}Ag0.7wt{\%}Cu$ 솔더와 Pt층의 시효처리에 따른 계면반응에 대한 연구를 수행하였다. $250^{\circ}C$에서 30 초간 리플로한 $Sn3.8wt{\%}Ag0.7wt{\%}Cu/Pt$시편과, $260^{\circ}C$에서 30초간 리플로한 $Sn0.7wt{\%}Cu/Pt$ 시편을 이용하여 125, 150, $170^{\circ}C$에서 25-121 시간동안시효처리 하였다. 시효처리 온도와 시간에 따른 계면 금속간화합물의 두께 및 형상변화를 주사전자현미경 (scanning electron microscopy, SEM), energy dispersive x-ray spectroscopy (EDS) 및 x-ray diffractometry (XRD)를 이용하여 분석하였다. 분석 결과 계면에서 $PtSn_4,\;PtSn_2$가 발견되었고, 이런 금속간화합물 성장은 확산에 의해 지배됨을 발견하였다. 시효처리 온도와 시간에 따른 금속간화합물의 두께 변화를 이용하여 각 솔더에서의 계면 금속간화합물의 생성 활성화 에너지를 구해본 결과 $Sn3.8wt{\%}Ag0.7wt{\%}Cu/Pt$는 145.3 kJ/mol, $Sn0.7wt{\%}Cu/Pt$는 165.1 kJ/mol의 값을 가지고 있었다.