Preparation of α-Al2O3 Nanoparticles by flame Spray Pyrolysis (ESP) of Microemulsion

마이크로에멀전의 화염분무열분해(ESP)에 의한 α-알루미나 나노입자의 제조

  • 이상진 (경남대학교 신소재공학부) ;
  • 전병세 (경남대학교 신소재공학부)
  • Published : 2004.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Nano-sized a-alumina with a narrow distribution was prepared by using Flame Spray Pyrolysis (FSP). The microemulsion of water in oil (W/O) was prepared to make ultrafine droplets for FSP process. Kerosene (fuel) as a continuos phase and Al(NO$_3$)$_3$$.$9$H_2O$ (oxidizer) aqueous solution as a dispersed phase were prepared for microemulsification. The microemulsion with dispersion stability was obtained by adjusting the composition of 80 vol% kerosene, 10 vol% aqueous solution, and 10 vol% emulsifying agent. Microemulsion was sprayed onto the flame by using two-fluid nozzle spray gun under the condition of 0.03 ㎫ air pressure. The synthesized products were $\alpha$-alumina phase with the size of 20 to 30 nm.

화염분무열분해(FSP) 공정을 이용하여 결정질의 좁은 입도분포를 가지는 $\alpha$-알루미나 나노입자를 제조하였다. 초미분의 액적을 형성시키기 위해 전구체 용액으로서 연료인 등유를 연속상으로 하고 산화제인 알루미늄 질산염 수용액을 분산상으로 하는 유중수적(W/O)형의 마이크로에멀전을 제조하였다 0.5M 농도의 알루미늄 질산염 수용액을 10vol%, 등유 80vol%, 그리고 유용성 유화제 10vol%를 혼합하여 안정한 분산상태를 가지는 마이크로에멀전을 제조한 후, 이류체 노즐 분무기를 사용하여 0.03㎫의 공기 압력으로 분무하여 화염에 직접 노출시켰다. 제조된 생성물은 20에서 30 나노미터의 균일한 크기를 가지는 $\alpha$-알루미나 상으로 확인되었다.

Keywords

References

  1. New Ceramics J.H.Park
  2. Special Publication of the Am. Ceram. Soc. Alumina as a Ceramic Material W.H.Gitzen
  3. Ceramics Raw Materials J.K.Lee
  4. Ph. D. Thesis Spray Combustion Synthesis Process for the Preparations of Nano-Sized Ultrafine Ceramic Powders S.J.Lee
  5. J. Kor. Ceram. Soc. v.28 no.10 Preparation of Spherical TiO₂Powders by Spray Pyrolysis Using Ultrasonic Atomization Technique J.H.Lee;H.J.Cho;S.J.Park
  6. Aerosol Processing of Materials T.T.Kodas;M.J.Hampden-Smith
  7. Special report of C & En., Am. Chem. Soc. Flame Synthesis of Fine Particles G.D.Ulrich
  8. J. Nano. Res. v.4 Homogeneous ZnO Nanoparticles by Flame Spray Pyrolysis T.Tani;L.Madler;S.E.Pratsinis https://doi.org/10.1023/A:1021153419671
  9. J. Aerosol Sci. v.8 The In-Flame-Reaction Method for Al₂O₃ Aerosol Formation M.Sokolowski;A.Sokolowska;A.Michalski;B.Gokieli
  10. Nano. Mater. v.8 Nanomaterial Powders and Deposits Prepared by Flame Spray Processing of Liquid Precursors J.Karthikeyan;C.C.Berndt;J.Tikkanen;J.Y.Wang;A.H.King;H.Herman https://doi.org/10.1016/S0965-9773(97)00066-4
  11. Aero. Sci. Tech. v.34 A Novel Aerosol Combustion Process for the High Rate Formation of Nanoscale Oxide Particles A.Kilan;T.F.Morse https://doi.org/10.1080/027868201300034880
  12. Aerosol Sci. Tech. v.27 no.2 Production of Nanometer-Sized Metal Oxide Particles by Gas Phase Reaction in a Free Jet.; 1. Experimetal System and Results R.S.Windler;S.K.Friedlander;K.E.J.Lehtinen https://doi.org/10.1080/02786829708965465
  13. Prog. Energy Combust. Sci. v.24 Flame Aerosol Synthesis of Ceramic Powders S.E.Pratsinis https://doi.org/10.1016/S0360-1285(97)00028-2
  14. J. Kor. Ceram. Soc. v.5 no.3 Microemulsion Processing of Lead Magnesium Niobate Powders W.B.Ng;J.Wang;S.C.Ng;L.M.Gan
  15. J. Kor. Ceram. Soc. v.5 no.3 Crystallographic and Magnetic Properties of Nanocrystlline Cobalt Ferrite Particles Y.Ahn;E.J.Choi;S.Kim
  16. J. Am. Ceram. Soc. v.82 no.4 Ultrafine Barium Titanate Powders via Microemulsion Processing Routes J.Wang;J.Fang;S.Ng;L.Gan;C.Chew;X.Wang;Z.Chen https://doi.org/10.1111/j.1151-2916.1999.tb01848.x
  17. Microemulsions : Theory and Practice L.M.Pric
  18. Mat. Res. Soc. Symp. Proc. v.73 Preparation of Ceramic Powders from Emulsions M.Akinc;K.Richardson https://doi.org/10.1557/PROC-73-99
  19. Mater. Trans. v.37 no.4 Synthesis and Formatin Mechanism of Ultrafine Spherical Al₂O₃Powders by Ultrasonic Spray Pyrolysis V.Jokanovic;D.J.Janackovic;A.M.Spasic;D.Uskokovic https://doi.org/10.2320/matertrans1989.37.627