Preparation of TiO2-SiO2 Sol and Its Photo-Catalyst Properties for High Temperatures

고온 소성용 TiO2-SiO2계 광촉매의 제조 및 특성

  • Published : 2004.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

TiO$_2$, SiO$_2$, and PBA(Pseudo Boehemite Alumina) sol were prepared by sol-gel process. The particle sizes of these sol exhibited uniform 10∼30 nm. As the amount of SiO$_2$ sol increased, the temperature of phase transition (from anatase phase to rutile phase) was raised temperature than $600^{\circ}C$, which attributed to the enhanced photocatalyst properties. Also, the anatase phase was obtained with very small amount of the rutile phase from the addition of SiO$_2$ (10∼30 wt%) at annealing temperature of 120$0^{\circ}C$. The specimen with 20 wt% SiO$_2$ sol exhibited the maximum photocatalyst properties. But, the specimen with PBA sol did not affect photocatalytic activity due to the presence of rutile phase.

졸겔 공정으로 안정한 TiO$_2$, SiO$_2$, PBA(Pseudo Boehemite Alumina) 졸을 제조하였다. 제조한 졸 용액은 비교적 균일한 10∼30nm의 입자크기를 나타내었다. TiO$_2$졸에 SiO$_2$졸의 첨가량이 증가함에 따라, anatase상에서 rutile 상으로 전이되는 상전이 온도를 $600^{\circ}C$ 이상으로 증가시켜 광분해 특성을 향상시켰다. 또한, TiO$_2$ 졸 용액에 SiO$_2$ 졸을 10∼30wt% 첨가하여 120$0^{\circ}C$ 이상의 고온 소성 후에도 anatase가 주된 상으로 소량의 rutile 상이 관찰되었다 또한 SiO$_2$20wt% 첨가 시, 최대의 광분해 특성을 나타내었다. 그러나, PBA 졸의 첨가는 첨가량에 관계없이 광분해 특성에 영향을 주지 않았다.

Keywords

References

  1. J. Mater. Sci. v.35 no.2 Crystal Structure and Optical Property of Ti$O-2$ Gels and Films Prepared from Tiedta Complexes as Titania Precursors T. Nishide;M. Sato;H. Hara https://doi.org/10.1023/A:1004731804075
  2. Surf. Sci. v.446 no.1-2 The Surface Structure of $TiO_2$(001) after High Temperature Annealing Studied by AFM, STM, and Optical Microscopy H. Norenberg;F. Dinelli;G. Briggs
  3. Thin Solid Films v.228 Microstructure and Optical Properties of Amorphous $TiO_2-SiO_2$ Composite Films Synthesized by Helicon Plasma Sputtering X. Wang;H. Masumoto;Y. Someno;T. Hirai https://doi.org/10.1016/0040-6090(93)90574-9
  4. Thin Solid Films v.359 Optical and Mechanical Properties of $TiO_2/SiO-2$/ Organically Modified Silane Composite Films Prepared by Sol-Gel Processing W. Que;Z. Sun;Y. Zhou;Y. L. Lam;Y. C. Chan;C. H. Kam https://doi.org/10.1016/S0040-6090(99)00746-4
  5. Thin Solid Films v.360 Reactive Sputter Deposition of Titania Dioxide R. Dannenberg;P. Greene https://doi.org/10.1016/S0040-6090(99)00938-4
  6. J. Kor. Ceram. Soc. v.36 no.7 Surface Modification of Mica Using Ti$O_2$ Prepared by Alkoxide Hydrolysis Method S. P. Han;Y. H. Yun;S. H. Lee;S. C. Choi
  7. J. Kor. Ceram. Soc. v.30 no.7 Preparation of Glass-Ceramics in $Li_2O-Al_2O_3-TiO_2-SiO_2$ System by Sol-Gel Technique (1) Preparation of Porous Monolithic Gel in $Li_2O-Al_2O_3-TiO_2-SiO-2$ System by Sol-Gel Method H. S. Cho;J. S. Yang;C. O. Kweon;H. H. Lee