Abstract
The a-Si：H TFTs decreasing parasitic capacitance of source-drain is fabricated on glass. The structure of a-Si：H TFTs is inverted staggered. The gate electrode is formed by patterning with length of 8 ${\mu}m∼16 ${\mu}m. and width of 80∼200 ${\mu}m after depositing with gate electrode (Cr) 1500 under coming 7059 glass substrate. We have fabricated a-SiN：H, conductor, etch-stopper and photoresistor on gate electrode in sequence, respectively. The thickness of these thin films is formed with a-SiN：H (2000 ), a-Si：H(2000 ) and n+a-Si：H (500). We have deposited n+a-Si：H ,NPR(Negative Photo Resister) layer after forming pattern of Cr gate electrode by etch-stopper pattern. The NPR layer by inverting pattern of upper gate electrode is patterned and the n+a-Si：H layer is etched by the NPR pattern. The NPR layer is removed. After Cr layer is deposited and patterned, the source-drain electrode is formed. The a-Si：H TFTs decreasing parasitic capacitance of source-drain has channel length of 8 ~20 ${\mu}m and channel width of 80∼200 ${\mu}m. And it shows drain current of 8 ${\mu}A at 20 gate voltages, Ion/Ioff ratio of 108 and Vth of 4 volts.
본 연구는 에치스토퍼를 기존의 방식과 다르게 적용하여 수소화 된 비정질 실리콘 박막 트랜지스터의 제조공정을 단순화하고, 박막 트랜지스터의 게이트와 소오스-드레인간의 기생용량을 줄인다. 본 연구의 수소화 된 비정질 실리콘 박막 트랜지스터는 Inverted Staggered 형태로 게이트 전극이 하부에 있다. 실험 방법은 게이트전극, 절연층 , 전도층, 에치스토퍼 및 포토레지스터층을 연속 증착한다. 스토퍼층을 게이트 전극의 패턴으로 남기고, 그 위에 n+a-Si：H 층 및 NPR(Negative Photo Resister)을 형성시킨다. 상부 게이트 전극과 반대의 패턴으로 NPR층을 패터닝하여 그것을 마스크로 상부 n+a-Si：H 층을 식각하고, 남아있는 NPR층을 제거한다. 그 위에 Cr층을 증착한 후 패터닝하여 소오스-드레인 전극을 위한 Cr층을 형성시켜 박막 트랜지스터를 제조한다. 이렇게 제조하면 기존의 박막 트랜지스터에 비하여 특성은 같고, 제조공정은 줄어들며, 또한 게이트와 소오스-드레인간의 기생용량이 줄어들어 동작속도를 개선시킬 수 있다.