Preparation of α-Al2O3 Platelets from Aluminum Hydroxides Gel

Aluminium Hydroxides Gel을 이용한 α-Al2O3 판상체의 제조

  • 박병기 (한국화학연구원 화학공정 연구센터) ;
  • 이정민 (한국화학연구원 화학공정 연구센) ;
  • 서동수 (충남대학교 재료공학) ;
  • 임광수 (스카이케미칼(주))
  • Published : 2004.08.01
Download PDF
⟨ Previous Next ⟩

Abstract

For preparation $\alpha$-Al$_2$O$_3$ platelets having 20 $\mu$m in average diameter and 0.2∼0.3 $\mu$m in thickness, we have prepared aluminum hydroxides gel by using aluminum sulfate and sodium sulfate as starting materials. In this study, we investigated the effect of the amount of sodium phosphate on particle size, morphology and thickness of $\alpha$-Al$_2$O$_3$ platelets. When sodium phosphate was not added to aluminum hydroxides gel, most of $\alpha$-Al$_2$O$_3$ platelets had hexagonal shape but the thickness was over 1.0 $\mu$m, and this sample was not adequate for pearlescent pigment. On the other hand, introduction of sodium phosphate caused an increase of aspect ratio (particle diameter/thickness) with a decrease in $\alpha$-Al$_2$O$_3$ platelet thickness.

평균입자크기가 20 ${\mu}$이고, 두께가 0.2∼0.3 ${\mu}m$인 ${\alpha}-Al_2O_3$ 판상체를 제조하기 위하여 전구물질로써 황산알루미늄과 황산나트륨을 사용하여 수산화알루미늄을 제조하였다. 이때 첨가되는 인산나트륨의 양이 ${\alpha}Al_2O_3$ 판상체의 입자크기, 형상, 그리고 두께에 어떠한 영향을 미치는지에 대하여 관찰하였다. 인산나트륨을 첨가하지 않았을 경우, 대부분의 ${\alpha}-Al_2O_3$ 판 상체가 육각판상모양을 띠고 있었으나 그 두께가 1.0 ${\mu}m$ 이상으로 진주안료 기질로는 적합하지 않았다. 반면, 인산나트륨이 첨가되었을 경우, ${\alpha}-Al_2O_3$ 판상체의 두께를 감소시켜 각형비를 증가시키는 현상을 초래하였다.

Keywords

References

  1. J. Kor. Ceram. Soc. v.39 no.10 Characteristics of Alumina Particles Synthesized by Microwave Heating S. W. Kim;S. H. Lee;J. H. Park;J. H. Kim;S. S. Park;H. C. Park https://doi.org/10.4191/KCERS.2002.39.10.1007
  2. J. Am. Ceram. Soc. v.84 no.3 Synthesis of Aluminum Oxide Platelets R. F Hill;R. Danzer;R. T. Paine https://doi.org/10.1111/j.1151-2916.2001.tb00692.x
  3. Physical and Chemical Aspects of Adsorbents and Catalysts Active Alumina B. C. Lippens;J. J. Steggerda
  4. J. Kor, Ceram. Soc. v.32 no.4 Effects of ${\alpha}$-$Al_2O_3$ Seeds and Alumina Sol on ${\alpha}$-Aumina Powder Derived from ${\gamma}$-$Al_2O_3$ K. R. Han;J. W. Jang;C. S. Lim;K. S. Hong
  5. J. Am. Ceram. Soc. v.77 no.11 Growth of ${\alpha}$-$Al_2O_3$ Platelets in the HF-${\gamma}$-$Al_2O_3$ System C. A. Shaklee;G. L. Messing https://doi.org/10.1111/j.1151-2916.1994.tb04534.x
  6. J. Mater. Res. v.14 no.12 Synthesis of ${\alpha}$-$Al_2O_3$ Platelets Using Sodium Sulfate Flux S. Hashimoto;A. Yamaguchi https://doi.org/10.1557/JMR.1999.0631
  7. J. Euro. Ceram. Soc. v.19 Formation of Porous Aggregations Composed of $Al_2O_3$ Platelets Using Potassium Sulfate Flux S. Hashimoto;A. Yamaguchi https://doi.org/10.1016/S0955-2219(98)00202-7
  8. J. Am. Ceram. Soc. v.81 no.6 Size Control of ${\alpha}$-Alumina Particles Synthesized in 1 ,4-Butanediol Solution by ${\alpha}$-Alumina and ${\alpha}$-Hermatite Seeding N. S. Bell;S.-B. Cho;J. H. Adair https://doi.org/10.1111/j.1151-2916.1998.tb02498.x
  9. Encyclopedia of Surface and Colloid Science v.1 Crystal Growth Kinetics and Mechanisms L. Brecevic;Arthur T. Hubbard(ed.)
  10. Introduction to Ceramics W. D. Kingery;H. K. Bowen;D. R. Uhlmann
  11. J. Crystal Growth v.75 Morphology of Corundum Crystallized by Heating Mixture of ${\eta}$-$Al_2O_3$ and $AlF_3$ K. Daimon;E. Kato https://doi.org/10.1016/0022-0248(86)90049-7
  12. J. Am. Ceram. Soc. v.83 no.6 Synthesis of Hydrated Aluminum Sulfate from Kaolin by Microwave Extraction S. S. Park;E. H. Hwang;B. C. Kim;H. C. Park https://doi.org/10.1111/j.1151-2916.2000.tb01390.x
  13. J. Am. Ceram. Soc. v.84 no.2 Molten Salt Synthesis of Calcium Hydroxyapatite Whiskers A. Cuneyt Tas https://doi.org/10.1111/j.1151-2916.2001.tb00653.x
  14. Yogyo-Kyakai-Shi(Japan) v.85 Sinterability of Alumina Powders Prepared in Different Processed from Hydrated Sulfate E. Kato;K. Dimon;A. Yamaguchi;T. Yamada; https://doi.org/10.2109/jcersj1950.85.979_134
  15. J. Kor. Ceram. Soc. v.35 no.10 The Rehydration Properties of Amorphous Alumina Powder in Low Water/Alumina Ratio B. K. Park;J. K. Suh;J. M. Lee;D. S. Suhr
  16. J. Kor Ceram. Soc. v.39 no.3 Preparaton of High-Capacity Ceramic Catalytic Support from Gibbsite B. K. Park;J. K. Suh;J. M. Lee;D. S. Suhr https://doi.org/10.4191/KCERS.2002.39.3.245
  17. J. Kor. Ceram. Soc. v.40 no.7 Preparation of Fe$_2O_3$M/TEX> Supported ${\gamma}$-Alumina Catalyst by Hydrothermal Method B. K. Park;J. M. Lee;D. S. Suhr https://doi.org/10.4191/KCERS.2003.40.7.683
  18. J. Kor. Ceram. Soc. v.40 no.8 Effect of CH$_3$COOH Concentration on Characteristics of Fc$_2O_3$ Supported ${\gamma}$-Alumina Catalyst by Hydrothermal Method B. K. Park;J. M. Lee;D. S. Suhr https://doi.org/10.4191/KCERS.2003.40.8.758