Abstract
Failure process, mode and strength of unidirectional composite single lap bonded joints were investigated experimentally with respect to bonding methods, those are, co-curing with and without adhesive and secondary bonding. The co-cured joint specimens without adhesive had the largest failure strength. Progressive failures along the adhesive layer occurred in the secondary bonded specimens. In the co-cured specimens with adhesive film which had better material strength and adhesion performance, delamination failure occurred and the joint strengths were less than those of secondary bonded specimens. Delamination failure did not occur in the secondary bonded specimens because of earlier crack growth and progressive failure in the adhesive layer. Therefore, failure strength of composite bonded Joints were not always proportionate to material strength and adhesion performance of the adhesive due to the weakness of delamination in composite materials. The effects of surface roughness, bondline thickness and fillets were also studied on secondary bonded specimens.
본 연구에서는 몇 가지 접합 방법에 따라 일방향 복합재료 단일 겹치기 접합 조인트의 파손 과정, 모드 및 강도를 실험적으로 평가하였다 접합 방법으로는 접착제 없는 동시성형, 접착제를 사용한 동시성형 및 이차 접합의 세 가지를 고려하였다 또한 이차 접합 조인트에서 몇 가지 파라미터의 영향도 살펴보았다. 접착제 없는 동시성형 시편은 가장 우수한 조인트 강도를 나타내었다. 이차접합 조인트에서는 접착제 층의 점진적인 파손이 발생하였다. 접착제의 재료 및 접합 강도가 상대적으로 강한 필름 접착제의 동시성형 조인트는 갑작스런 층간분리 파손이 발생하였으며 이차 접합 조인트보다 더 낮은 파손 강도를 나타내었다. 이차 집합 조인트에서 층간분리 파손이 발생하지 않은 것은 접착제 층에서의 균열 진전 및 점진적 파손이 층간분리 파손을 방지한 것으로 보인다. 따라서 복합재료 접합 조인트의 파손 강도는 접착제의 재료 강도 또는 접착 성능과 항상 비례하지 않으며 이것은 복합재료가 층간 분리 파손에 약하기 때문이다.