Al 2024-T3재의 Crack Opening Point의 평가에 관한 연구

A Study on Evaluation of Crack Opening Point in Al 2024-T3 Material

  • 최병기 (조선대학교 공과대학 기계공학과) ;
  • 장경천 (한국생산기술연구원)
  • 발행 : 2004.06.01
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

This paper aims to analyze fatigue fracture mechnisms with high strength aluminum alloys, which are widely used in vehicles or airplanes to prevent accidents. Usefulness of the crack opening point was proposed by using an effective stress intensity facor when evaluating the fatigue crack propagaion rate. Therefore an exact crack opening ratio can be measured for a more exact fatigue crack propagation rate. It is found that the fatigue crack propagation rate was valid within the range of experimentation as an effective stress intensity factor. Summarizing the results are as follows in this paper ; (1) It is found that the value of the crack opening ratio is constant at the rear of the specimen, U'=0.25 at the crack mouth and U'=0.45 at the crack tip, respectively regardless of the stress ratio. (2) The crack opening ratio is different according to measurement locations. The crack opening ratio value was measured at the crack mouth by a clip gage or measured behind the specimen by a strain gage. It is found that the crack opening ratio value is more accurate that any other measuring test for evaluating the crack propagation ratio test by effective stress intensity factor.

키워드

참고문헌

  1. Elber W., 'The significance of Fatigue Crack Closure', ASTM STP 486, pp. 230-242, 1971
  2. 小林英男, 涉谷榮一, '"疲勞き裂進展の彈塑性破壞力學にする評價', 材科, 第29卷, 第325號, pp. 1049-1055, 1980
  3. Elber W., 'Fatigue Crack Closure Under Cyclic Tension', Engineering Fracture Mechanics Vol. 2, pp. 37-45, 1970 https://doi.org/10.1016/0013-7944(70)90028-7
  4. 菊川眞,城野政弘, 'ランダム含む正常動荷重下の疲勞き裂開閉口學動とき裂進展速度の推定法(第2報, 高進展速度領域への張), 日本機械學會論文集, 第49卷, 第439號, pp. 278-285, 1983
  5. Haenny L, and Dickson J. I., 'Comments on the Experimental Evaluation of Fatigue Crack Closure', International Journal of Fracture, Vol. 16. pp. R121-R125, 1980 https://doi.org/10.1007/BF00013390
  6. 小林英男, 小川武史, 'SFVV3鋼の疲勞き裂開閉口の實測と下限界特性の評價', 日本機械學會論文集, 第50卷, 第451號, pp. 309-319, 1984
  7. 西谷弘信, ''除荷確彈性ユンプライアニス法に開する考奈', 日本機械學會論文集, 第51卷, 第465號, pp. 1463-1441, 1985
  8. Elber W., 'Equivalent Constant Amplitude Concept for Crack Growth under Spectrum loading', ASTM STP 595, pp. 236-250, 1976
  9. Schijve J., 'Observations on the Prediction of Fatigue Crack Growth Propagation Under Variable Amplitude Loading', ASTM STP 595, pp. 3-23, 1976
  10. Schijve J., 'Significance of Fatigue Cracks in Micro Range and Macro Range', ASTM STP 415, pp. 415-457, 1967
  11. Schijve J., 'Four Lectures on Fatigue Crack Growth', Engineering Fracture Mechanics, Vol. 11, pp. 167-221, 1979 https://doi.org/10.1016/0013-7944(79)90038-9
  12. Vazquez J. A., 'Experimental Results on Fatigue Crack Closure for Two Aluminum Alloys', Engineering Fracture Mechanics, Vol. 12, pp. 231-240, 1979 https://doi.org/10.1007/BF00036980
  13. ASTM E647-83, 'Constant Load Amplitude Fatigue Crack Growth Rates Above 10-8m/cycle', pp. 711-731, 1984