Abstract
In construction site, there are some occasions where concrete under initial curing is being affected by nitration from nearby vibration sources. To study these effects, in this paper, strength characteristics of concrete specimens subjected to continuous vibration up to 12 hours in vertical direction after concrete placement were observed. And through the vibration time control experiment where a number of time combinations consisted of times before and after applying vibration during initial curing period were used as experimental parameters, possibility of concrete strength improvement was investigated. From the experimental results, it could be seen that the concrete strengths were mostly decreased due to the increase of vibration velocity during initial curing period. But fluctuation ratio of concrete strength did not have any close correlations with the vibration times. And results of vibration time control experiment showed that if times before applying vibration sustains at least more than 3 hours, subsequent vibrations after that hours do not affect the concrete strength in any unfavorable ways.
건설현장에서 초기양생 중에 있는 콘크리트는 주위의 진동원으로부터 진동의 영향을 받는 경우가 자주 발생한다. 이러한 영향을 분석하기 위하여, 본 연구에서는 콘크리트 타설 후 최대 12시간까지 수직방향으로 연속진동을 받은 콘크리트 공시체의 강도 특성을 조사하였다. 또한 초기양생기간 중 진동을 받기 전 시간(진동가력 전 시간)과 진동을 받는 시간(진동가력시간) 간격들의 여러 조합에 관한 실험을 통하여 진동시간 제어에 따른 콘크리트 강도 개선의 가능성을 조사하였다. 실험결과, 초기양생중 수직진동의 영향을 받으면 강도는 진동속도가 증가함에 따라 강도의 감소율이 전반적으로 증가하는 경향을 보여주었으나, 진동가력시간에 따라서는 일정한 경향을 나타내지 않음을 알 수 있었다. 또한 진동시간 제어 실험에서 진동을 받은 콘크리트 공시체들의 강도 증감률을 조사해본 결과, 진동가력 전 시간이 3시간 이상만 유지된다면 이 이후의 진동가력은 강도 감소 등의 불리한 영향을 주지 않는다고 판단되었다.