Influence of Styrene Contents on Retraction Behaviors of SBR Vulcanizates

SBR 가황물의 회복 거동에 미치는 스티렌 함량의 영향

  • Published : 2005.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

Influence of the styrene content on the retraction behaviors of SBR vulcanizates was studied. SBRs with different styrene contents of 15 and 21 wt% were used. The vulcanizate with low styrene content started to recover at lower temperature than that with high one. The recovery rate of the vulcanizate with low styrene content was slower than that with high one. The recovery difference between the two vulcanizates with different styrene contents was larger for the carbon black-filled vulcanizates than for the silica-filled ones. The experimental results were explained with the glass transition temperature and modulus.

스티렌 함량이 SBR 가황물의 회복 거동에 미치는 영향에 대해 연구하였다. 스티렌 함량이 15와 21 wt%인 SBR을 사용하였다. 스티렌 함량이 적은 가황물이 스티렌 함량이 많은 가황물에 비해 더 낮은 온도에서 회복하기 시작하였으며, 스티렌 함량이 적은 가황물의 회복 속도가 스티렌 함량이 많은 가황물보다 느렸다. 두 가황물 간의 회복 차이는 카본블랙으로 보강된 가황물이 실리카로 보강된 것보다 컸다. 실험 결과는 유리전이온도와 모듈러스로 설명하였다.

Keywords

References

  1. J. E. Mark, 'Rubber elasticity', J. Chem. Edu., 58, 898 (1981).
  2. B. Erman, and J. E. Mark, 'Rubber-like elasticity', Annu. Rev. Phys. Chem., 40, 351 (1989)
  3. J. E. Mark, 'Molecular aspects of rubberlike elasticity', Angew. Makromol. Chem., 202/203, 1 (1992)
  4. W. L. Hergenrother and J. M. Doshak, 'Tensile retraction measurements. V. The effect of carbon black on the crosslink density of cured rubber', J Appl. Polym. Sci., 48, 1621 (1993)
  5. J. H. Yun and T. H. Kim, 'A study on the low temperature retraction of NR', Elastomer, 35, 303 (2000)
  6. S.-S. Choi, B.-H. Park, W. S. Kim, and W. D. Kim, 'Influence of silane coupling agent on retraction behaviors of NR vulcanizates reinforced with carbon black and clay', Elastomer, 40, 112 (2005)
  7. S.-S. Choi, 'Influence of polymer-filler interactions on retraction behaviors of natural rubber vulcanizates reinforced with silica and carbon black', J Appl. Polym. Sci., in press