Cu 미세 배선을 위한 무전해 Ni-B 확산 방지막의 Cu 확산에 따른 상변태 거동

Phase Transformation by Cu Diffusion of Electrolessly Deposited Ni-B Diffusion Barrier for Cu Interconnect

  • Choi J. W. (Div. of Materials Science and Engineering, hanyang Univ.) ;
  • Hwang G. H. (Div. of Materials Science and Engineering, hanyang Univ.) ;
  • Song J. H. (Div. of Materials Science and Engineering, hanyang Univ.) ;
  • Kang S. G. (Div. of Materials Science and Engineering, hanyang Univ.)
  • 발행 : 2005.11.01

초록

The phase transformation of Ni-B diffusion barrier by Cu diffusion was studied. The Ni-B diffusion barrier, thickness of 10(Inn, was electrolessly deposited on the electroplated Cu interconnect. The specimens were annealed either in Ar atmosphere or in $H_2$ atmosphere from $300^{\circ}C\;to\;800^{\circ}C$ for 30min, respectively. Although the Ni-B coated specimens showed the decomposition of $Ni_3B$ above $400^{\circ}C$ in both Ar atmosphere and $H_2$ atmosphere, Ni-B powders did not show the decomposition of $Ni_3B$. The $Ni_3B$ was decomposed to Ni and B in hi atmospherr: and the metallic Ni formed the solid solution with Cu and the free B was oxidized to $B_2O_3$. However, both the boron hydride and free B were not observed in the diffusion barrier after the annealing in $H_2$ atmos There. These results revealed that the decomposition of $Ni_3B$ by Cu made the Cu diffusion continued toward the Ni-B diffusion barrier.

키워드

참고문헌

  1. B. Li, T. D. Sullivan, T. C. Lee, D. Badami, Microelectron. Reliab., 44, 365 (2004) https://doi.org/10.1016/j.microrel.2003.11.004
  2. A. K. Stamper, M. B Fushelier, X. Tian, 'Advanced wiring RC delay issues for sub-0.25-micron general CMOS' in 'Proceedings of Int. Interconnect Tech. Conf. (IITC)', 62 (1998) https://doi.org/10.1109/IITC.1998.704752
  3. S. P. Murarka, Solid State Technol., 3, 83-90 (1996) https://doi.org/10.1016/0038-1101(95)00093-9
  4. T. L. Alford, Y. Zeng, P. Nguyen, L. Chen and J. W. Mayer, Microelectron. Eng., 55, 389 (2001) https://doi.org/10.1016/S0167-9317(00)00472-X
  5. K. Yamashita and S. Odanaka, IEEE T. Electron Dev., 47, 90 (2000) https://doi.org/10.1109/16.817572
  6. X. W. Lin and D. Pramanlk, Solid State Technol., 63 (1998)
  7. J. R. Lloyd and J. J. Clement, Thin Solid Films, 262, 135 (1995) https://doi.org/10.1016/0040-6090(94)05806-7
  8. D. S. Gardner, J. Onuki, K. Kudoo, Y. Misawa and Q. T. Vu, Thin Solid Films, 26, 104 (1995) https://doi.org/10.1016/0040-6090(95)05838-9
  9. S. P. Murarka, I. V. Verner, and R. J. Gutmann, 'Copper Fundamental Mechanism for Microelectronic Applications', Wiley, New York, (2000)
  10. S. T. Lin, Y. L. Kuo and C. Lee, Appl. Surf. Sci., 220, 349 (2003) https://doi.org/10.1016/S0169-4332(03)00871-7
  11. H. K. Kang, I. Asano, C. Ryu and S. S. Wong, in 1993 VMIC Conf. Proc., 223 (1993)
  12. H. Kizil and C. Steinbrucbel, Thin Solid Films, 449, 158 (2004) https://doi.org/10.1016/j.tsf.2003.10.111
  13. H. Ono, T. Nakano and T. Ohta, Appl. Phys. Lett., 64, 151 (1994) https://doi.org/10.1063/1.111875
  14. S. Saito, K. Matsuda, K. Nishizawa and K. Sakiyama, Mater. Res. Soc., 319 (1987)
  15. S. Q. Wang, I. Raaijmakers, B. J. Burrow, S. Suthar, S. Redkar and K. B. Kim, J. Appl. Phys., 68, 5176 (1990) https://doi.org/10.1063/1.347059
  16. K. Holloway, P. M. Fryer, C. Cabral Jr., J. M. E. Harper, P. J. Bailey and K. H. Kelleher, J. Appl. Phys., 71, 5433 (1992) https://doi.org/10.1063/1.350566
  17. J. Imahori, T. Oku and M. Murakami, Thin Solid Films, 301, 142 (1997) https://doi.org/10.1016/S0040-6090(97)00057-6
  18. M. Paunovic, P. J. Bailey, R. G. Schad and D. A. Smith, J. Electrochem. Soc., 141(7), 1843 (1994) https://doi.org/10.1149/1.2055015
  19. J. W. Choi, S. J. Hong, H. Y. Lee and S. G. Kang, Kor. J. Mat. Res., 13(2), 101 (2003) https://doi.org/10.3740/MRSK.2003.13.2.101
  20. H. Zhang, X. Zhang and Y. K. Zhang, Plat. and Surf. Finish., 80(4), 80 (1993)
  21. T. V. Gaevskaya, I. G. Novotortseva and L. S. Tsybulskaya, Met. Finish., 94, 100 (1996) https://doi.org/10.1016/0026-0576(96)83649-X
  22. K. Masui, Met. Finish., 84, 33 (1986)
  23. T. S. N. Sankara Narayanan and S. K. Seshadri, J. Alloys and Comp., 365, 197 (2004) https://doi.org/10.1016/S0925-8388(03)00680-7
  24. H. Li, H. Li and J. F. Deng, Mater. Lett., Aug., 41 (2001) https://doi.org/10.1016/S0167-577X(00)00410-9