The Characteristics of Wear Resistance of Cu-TiB2 Composites Reinforced by TiB2 Powders

TiB2 분말로 강화된 Cu-TiB2 복합재료의 내마모특성

  • Lee Tae-Woo (Department of Materials Science and Engineering, Seoul National University of Technology) ;
  • Choi Jong-Un (Department of Materials Science and Engineering, Seoul National University of Technology) ;
  • Kang Kae-Myung (Department of Materials Science and Engineering, Seoul National University of Technology)
  • 이태우 (서울산업대학교 신소재공학과) ;
  • 최종운 (서울산업대학교 신소재공학과) ;
  • 강계명 (서울산업대학교 신소재공학과)
  • Published : 2005.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

In this study the effect of the content of $TiB_2$ on wear properties was investigated. $Cu-TiB_2$ composites have been fabricated by hot extrusion. Sliding wear tests were peformed by a pin-on-disk type wear test machine under dry condition and loads varied with from 20N to 80N at sliding speed 3.5Hz. The test results showed that the wear losses and the friction coefficients decreased with increasing $Cu-TiB_2$ volume fraction and increasing the size of $Cu-TiB_2$ particle. Wear property of $10{\mu}m,\;5 vol\%\; TiB_2$ specimen was excellent all of the wear specimens. It is thought that the increase of plastic flow resistivity due to uniform distribution of $10{\mu}m,\;5 vol\%\; TiB_2$ wear specimen would improve wear property. The worn surface and wear debris were examined by optical microscope and scanning electron microscope.

Keywords

References

  1. Fehim Findik, Huseyin Uzun, Mterials and design, 24, 489 (2003) https://doi.org/10.1016/S0261-3069(03)00125-0
  2. Y. J. Kwon, M. Kobashi, T. Choh and N. Kanetake, Scripta Materialia, 50, 577, (2004) https://doi.org/10.1016/j.scriptamat.2003.11.056
  3. J. S. Lee, N. J. Kim, J. Y. Jung, E. S. Lee and S. A. Scripta Materialia, 39(8), 1063, (1998) https://doi.org/10.1016/S1359-6462(98)00246-2
  4. Q. Xu, X. Zhang, J. Han, X. He and V. L. Kvanin, Materials letters, 57, 4439 (2003) https://doi.org/10.1016/S0167-577X(03)00338-0
  5. J. N. Kim, J. U. Choi and K. M. Kang. Korea Journal of Materials Research, 15(1), 61 (2005) https://doi.org/10.3740/MRSK.2005.15.1.061
  6. M. Lopez, D. Corredor, C. Camurri, V. Vergara and J. ？Jimenez, Material Characterization, 55, 252 (2005) https://doi.org/10.1016/j.matchar.2005.04.006
  7. S. C. Tjong and K. C. Lau, Composites Science and Technology, 60, 1141 (2000) https://doi.org/10.1016/S0266-3538(00)00008-7
  8. X. L. Kong, Y. B. Liu and L. J. Qiao, Wear, 256, 747(2004) https://doi.org/10.1016/S0043-1648(03)00528-3
  9. J. P. Tu, W. Rong, S. Y. Guo and Y. Z. Yang, Wear, 255, 832 (2003) https://doi.org/10.1016/S0043-1648(03)00115-7
  10. Y. Leprince-Wang, K Han, Y. Huang and K. Yu-Zhang, Materials Science and Engineering, A351, 214 (2003) https://doi.org/10.1016/S0921-5093(02)00855-9
  11. T.-H. Kim and J.-S. Lee, Journal of Korean Powder Metallurgy Instisute, 1, 174 (1994)
  12. J.-L. Liu, E.-D. Wang, Z.-Y. Liu, L.-x. Hu and W.-B. Fang, Materials Science and Engineering, A382, 301 (2004) https://doi.org/10.1016/j.msea.2004.04.074
  13. Z. Zhang, R. Sandstrom and L. Wang, Journal of Materials Processing Technology, 152, 131 (2004) https://doi.org/10.1016/j.jmatprotec.2004.03.025
  14. D. Lou, J. Hellman, D. Luhulima, J. Liimatainen and V. K. Lindroos, Materials Science and Engineering, A340, 155 (2003) https://doi.org/10.1016/S0921-5093(02)00173-9
  15. K. M. Kang and J. T. Song, Wear, 140, 119 (1990) https://doi.org/10.1016/0043-1648(90)90126-U
  16. Z. Y. Ma and S. C. Tjong, Materials Science and Engineering, A284, 70 (2000) https://doi.org/10.1016/S0921-5093(00)00797-8
  17. K. M. Kang and J. U. Choi, Korea Journal of Materials Research, 14(1), 74 (2004).
  18. B. K. Prasad, wear, 257, 110 (2004) https://doi.org/10.1016/j.wear.2003.10.021
  19. K. M. Kang, 'A Metallurgical Study on the Wear Property and Weldability of High Carbon Cr- Ti Alloy Rail Steel', 12, Hanyang Univ., Thesis for Ph.D of Engineering, (1989)