PZT/LSMO/Pt Thin-Film by Pulse Laser and Sol-Gel Deposition

PZT/LSMO/Pt에 대한 펄스레이저 및 졸겔법에 의한 증착연구

This work is to present each properties and the interfacial characterization between PZT layer and LSMO layer of PZT/LSMO/Pt. LSMO thin film grown by KrF(248 nm) excimer lasers are used in pulsed in pulsed laser deposition(PLD). PZT coposites thin films were deposited by spin coating using a commercial resist spinner. LSMO thin film by deposition oxygen pressure 125 mtorr have rhombohedral structure on Pt(111) substrate. The PZT/LSM/Pt pre-orientate to [111] direction. The final thin films were shown that magnetic and electric property was typical value, respective. We report that the lattice between the PZT/LSMO thin film and the substrate plays a very important role and may control to another effects.

강자성, 초거대자기저항체인 $La_{0.67}Sr_{0.33}MnO_{3}$ 타겟을 이용하여 248nm의 파장을 갖는 KrF 엑시머 레이저를 사용한 PLD법으로 박막으 제작하고, 강유전체 물질인 $PbZr_{0.52}Ti_{0.48}O_{3}$ 물질을 spin coating 방법으로 제조하였다. Pt 기관(111)위에 125 mtorr의 산소분압으로 증착한 rhombohedral 구조를 갖는 LSMO 박막을 증착하고 그 위에 PZT 물질을 증착한 결과 LSMO, PZT en 물질 모두 단일상으로 [111]방향으로서의 성장하였음을 알 수 있었다. AFM(atomic force micrscope) data 및 SEM(scanning electron microscope) data를 바탕으로 매우 균질한 박막을 얻었음을 알 수 있었으며, 이때의 자기적 성질 및 전기적 성질은 각각 강자성적인 성질 및 강유전체적인 성향을 나타내었다. 이러한 결과를 가지고 박막증착에 있어서 서로간의 결정구조가 미치는 영향과 다른 경향에 대한 조절이 가능함을 알 수 있었다.