Physical and Mechanical Properties of Polymer Concrete Using Recycled Aggregate

재생골재를 사용한 폴리머 콘크리트의 물리·역학적 특성

This study was performed to evaluate the physical and mechanical properties of polymer concrete using unsaturated polyester resin, initiator, heavy calcium carbonate, crushed gravel, recycled coarse aggregate, silica sand and recycled fine aggregate. The unit weight, compressive strength, flexural strength and dynamic modulus of elasticity were decreased with increasing the content of recycled aggregate. The unit weight, compressive strength, flexural strength and dynamic modulus of elasticity were showed in $2,127{\sim}2,239kg/m^3$, 80.5~88.3MPa, 19.2~21.5MPa and $254{\times}10^2{\sim}288{\times}10^2MPa$ at the curing age 7 days, respectively. Therefore, these recycled aggregate can be used for polymer concrete.

이 연구는 현재 생산되고 있는 재생굵은골재와 재생잔골재를 폴리머 콘크리트 제조에 사용하기 위하여 불포화 폴리에스테르 수지, 개시제, 재생굵은골재, 쇄석, 재생잔골재, 규사, 탄산칼슘을 사용한 폴리머 콘크리트에 대한 물리 역학적 특성을 구명한 것으로서, 이 연구를 통해 얻어진 결과를 요약하면 다음과 같다. 1. 단위용적중량은 $2,127{\sim}2,239kg/m^3$의 범위로써 쇄석을 사용한 폴리머 콘크리트의 단위용적중량 $2,165{\sim}2,282kg/m^3$과 거의 유사하였고, 재생골재의 치환률이 증가할수록 감소하는 경향을 나타내었다. 2. 압축강도는 80.5~88.3 MPa의 범위로써, 쇄석을 사용한 폴리머 콘크리트의 압축강도 84.5~89.2 MPa에 비하여 1~2%정도 감소하였으며, 재생잔골재를 사용한 경우가 규사를 사용한 경우에 비하여 압축강도가 크게 나타나는 경향을 보였다. 3. 휨강도는 19.2~21.5 MPa의 범위로써, 쇄석을 사용한 폴리머 콘크리트의 휨강도 20.2~22.4 MPa에 비하여 4%정도 감소하였으며, 재생골재의 사용량이 증가할수록 휨강도는 감소하였다. 4. 동탄성계수는 $254{\times}10^2{\sim}288{\times}10^2MPa$의 범위로, 쇄석을 사용한 폴리머 콘크리트의 동탄성계수 $267{\times}10^2{\sim}294{\times}10^2MPa$보다 2~4%정도 감소되었으며, 재생골재의 사용량이 증가할수록 감소하였다. 5. 재생굵은골재와 재생잔골재를 사용한 폴리머 콘크리트를 개발하여 활용할 경우, 건설폐기물의 경제적이고 환경적인 처리가 가능할 것으로 기대되며, 고부가 가치의 환경친화적인 건설재료가 될 것으로 판단된다.