Abstract
A stoichiometric mixture of evaporating materials for $AgGaSe_2$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $AgGaSe_2$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy(HWE) system. The source and substrate temperatures were $630^{\circ}C\;and\;420^{\circ}C$, respectively. The temperature dependence of the energy band gap of the $AgGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=1.9501eV-(8.79x10^{-4}eV/K)T^2(T+250K)$. After the as-grown $AgGaSe_2$ single crystal thin films was annealed in Ag-, Se-, and Ga-atmospheres, the origin of point defects of $AgGaSe_2$ single crystal thin films has been investigated by the photoluminescence (PL) at 10K. The native defects of $V_{Ag},\;V_{Se},\;Ag_{int},\;and\;Se_{int}$ obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Ag-atmosphere converted $AgGaSe_2$ single crystal thin films to an optical p-type. Also, we confirmed that Ga in $AgGaSe_2$/GaAs did not form the native defects because Ga in $AgGaSe_2$ single crystal thin films existed in the form of stable bonds.
[$AgGaSe_2$] 단결정 박막을 수평 전기로에서 합성한 $AgGaSe_2$ 다결정을 증발원으로하여, hot wall epitaxy(HWE) 방법으로 증발원과 기판(반절연성-GaAs(100))의 온도를 각각 $630^{\circ}C,\;420^{\circ}C$로 고정하여 성장하였다. 이때 단결정 박막의 결정성은 광발광 스펙트럼과 이중결정 X-선 요동곡선(DCRC)으로 부터 구하였다. $AgGaSe_2$의 광흡수 스펙트럼으로부터 구한 온도에 의존하는 에너지 밴드갭 $E_g(T)$는 Varshni 공식에 fitting한 결과 $E_g(T)=1.9501eV-(8.79x10^{-4}eV/K)T^2(T+250K)$를 잘 만족하였다. 성장된 $AgGaSe_2$ 단결정 박막을 Ag, Ga, Se 분위기에서 각각 열처리하여 10K에서 photoluminescience(PL) spectrum을 측정하여 점 결함의 기원을 알아보았다. PL 측정으로 부터 얻어진 $V_{Ag},\;V_{Se},\;Ag_{int}$, 그리고 $Se_{int}$는 주개와 받개로 분류되어졌다. $AgGaSe_2$ 단결정 박막을 Ag 분위기에서 열처리하면 p형으로 변환됨을 알 수 있었다. 또한, Ga 분위기에서 열처리하면 열처리 이전의 PL 스펙트럼을 보이고 있어서, $AgGaSe_2$ 단결정 박막에서 Ga은 안정된 결합의 형태로 있기 때문에 자연 결함의 형성에는 관련이 없음을 알았다.