The study of Ag coated silica composite preparation by chemical method and their characteristics

화학적 방법에 의한 Ag coated silica 복합체의 제조 및 그 특성에 대한 연구

  • Published : 2006.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

Well dispersed uniform silver coated silica was prepared by chemical liquid method. The optimum conditions for preparation of the silver coated silica were as follows: alkaline solution, reaction temperature of $100^{\circ}C$, reaction time of 2 hrs, and amount of Ag of 5wt%. It was found that the prepared silver coated silica were far infrared emissivity of $0.916{\sim}0.918$ and antimicrobial effect of 99.9%.

화학적 방법에 의해 액상에서 실버가 잘 분산된 Ag coated silica를 제조하고 이를 평가하였다. Ag coated silica를 제조하기 위한 치적조건은 알카리 용액에서 반응온도 $100^{\circ}C$, 반응시간 2시간, 실버 코팅양은 5 wt%였다. 제조된 Ag coated silica는 실버가 응집되지 않은 일정한 크기의 단분산 실버가 실리카 표면에 균일하게 코팅되었으며, 윈적외선 방사율 $0.916{\sim}0.918$ 및 항균력 99.9%를 나타내었다.

Keywords

References

  1. M. Iwata, K. Adachi, S. Furukawa and T. Amakawa, 'Synthesis of purified AIN nano powder by transferred type arc plasma', Appl. Phys. 37 (2004) 1041
  2. T. Strachowski, E. Grzanka, B. Palosz, L. Slusarski and W. Lojkowski, 'Microwave driven hydrothermal synthesis of zinc oxide nanopowders', Solid State Phenomena 94 (2003) 189 https://doi.org/10.4028/www.scientific.net/SSP.94.189
  3. S. Shibata, K. Aoki, T. Yano and M. Yamane, 'Preparation of silica microspheres containing Ag nanoparticles', Journal of Sol-Gel Science and Technology 11(3) (1998) 279 https://doi.org/10.1023/A:1008610413657
  4. J.L. Delplancke, O. Bouesnard, J. Reisse and R.Winand, Mater. Res. Soc. Symp. Proc. 451 (1997) 383
  5. U. Schubert, Chern. Mater. 13 (2001) 3487 https://doi.org/10.1021/cm001258r
  6. Z.-R. Huang and D. Jiang, 'Nickel-alumina nanocomposite powders prepared by novel in situ chemical reduction', J. Mater. Res. 17(12) (2002) 3177 https://doi.org/10.1557/JMR.2002.0459
  7. S.G. Deng and Y.S. Lin, 'Sol-gel preparation and properties of Alumina adsorbents for gas separation', AIChE Journal 41(3) (2004) 559 https://doi.org/10.1002/aic.690410314
  8. A. Kumbhar and G. Chumanov, 'Synthesis and characterization of titania-coated silver nanoparticles', J. of Nanoscience and Nanotechnology 4(3) (2004) 299 https://doi.org/10.1166/jnn.2004.032
  9. C. Wang, Z. Ma and Z. Su, 'Synthesis and self-assembly of ilica-coated anisotropic gold nanoparticle films', Nanotechnology 17 (2006) 1819 https://doi.org/10.1088/0957-4484/17/8/002
  10. D.B. Zhang, H.M. Cheng, J.M. Ma, YP. Wang and X.Z. Gai, 'Synthesis of silver-coated silica nanoparticles in nonionic reverse micelles', Journal of Materials Science Letters 20(5) (2001) 439 https://doi.org/10.1023/A:1010906615079
  11. Z. Chen, X. Chen, L. Zheng, T. Gang, T. Cui, K. Zhang and B. Yang, 'A simple and controlled method of preparing uniform Ag midnanoparticles on Tollens-soaked silica spheres', Colloid Interface Sci. 285(1) (2005) 146 https://doi.org/10.1016/j.jcis.2004.11.056
  12. K. Kurihara, C. Rockstuhl, T. Nakano, T. Arai and J. Tominaga, 'The size control of silver nano-particles in $SiO_{2}$, matrix film', Nanotechnology 16 (2005) 1565 https://doi.org/10.1088/0957-4484/16/9/026