Abstract
Specimens with fillet-welded lap joints were fabricated from 20 mm, 60 mm, and 82 mm thick steel plates produced by Thermo Mechanical Control Process. The designed sizes of filet welds were betwen 6 mm and 16 m. The welds' axes were parallel with or perpendicular to the direction of loading or a combination of them. Specimens were axialy loaded in tension and the strength of fillet-welded joints were measured. Test results showed that the strengths of filet-welded joints are higher than the nominal strengths calculated for all the cases tested, and also approximately on the same level regardless of plate thickness and fillet weld size. Especially, the specimens with weld size les than that required by Korean design rules showed no visible defects on welds and also no str ength reduction.
최근 고성능 대형 강구조물에 많이 적용되고 있는 TMC 강재에 대해 두께 20m, 60m, 82m의 후판을 6m~16mm의여러 용접치수로 필릿용접하여 겹이음부가 있는 시험체를 제작하고, 인장시험을 통하여 필릿용접부의 강도를 측정하였다. 측정된 필릿용접부의 강도는 모재의 두께, 용접 치수, 용접축에 대한 힘의 작용방향 등을 달리한 모든 경우에 설계기준에서 적용하고 있는 강도 계산식에 의한 공칭강도의 값보다 더 큰 것으로 나타났다. 특히 60mm와 82mm 두께의 모재에 대해 국내도 로교설계기준에서 요구하고 있는 최소 용접치수보다 더 작은 용접치수를 적용한 경우에도 시험체 제작과정에 용접의 어려움이나 용접부의 결함, 균열 등이 발견되지 않았으며, 용접부의 강도도 다른 경우와 거의 동일한 수준인 것으로 나타났다.