Superparamagnetic Properties off Zn0.5Ni0.5Fe2O4 Nanoparticles

나노입자 Zn0.5Ni0.5Fe2O4 초상자성 성질 연구

  • Lee, Seung-Wha (Department of Electronic Engineering, Chungju National University)
  • 이승화 (충주대학교 전자공학과)
  • Published : 2006.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

[ $Zn_{0.5}Ni_{0.5}Fe_2O_4$ ] nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, SEM, and Mossbauer spectroscopy, VSM. $Zn_{0.5}Ni_{0.5}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ has spinel structure and behaved superparamagnetically at room temperature. The estimated size of superparammagnetic $Zn_{0.5}Ni_{0.5}Fe_2O_4$ nanoparticle is around 7 nm. The hyperfine fields of the A and I patterns at 4.2 K were found to be 510 and 475 kOe, respectively. The blocking temperature $(T_B)$ of superparammagnetic $Zn_{0.5}Ni_{0.5}Fe_2O_4$ nanoparticle is about 90 K. The magnetic anisotropy constant and relaxation time constant of $Zn_{0.5}Ni_{0.5}Fe_2O_4$ nanoparticle were calculated to be $K=1.6\times10^6erg/cm^3$.

졸-겔법을 이용하여 나노 입자 $Zn_{0.5}Ni_{0.5}Fe_2O_4$를 제조하여 x선 회절법(XRD) 및 주사전자현미경(SEM) 측정을 통하여 결정학적 특성 및 입자의 크기를 연구하였으며, 제조된 나노 입자의 초상자성 성질을 Mossbauer분광법, 진동시료 자화율 측정기(VSM)를 이용하여 연구하였다 XRD및 SEM의 측정으로부터 열처리 온도가 $300^{\circ}C$에서 순수한 cubic spinel구조를 가지며, 이 때 열 처리한 시료의 평균입자 크기는 7nm인 균일한 구형상 임을 알 수 있었다 Mossbauer분광실험으로 $300^{\circ}C$에서 열처리한 입자가 상온에서 초상자성의 특성을 가지고 있음을 알 수 있었으며, 4.2K에서의 초미세자기장은 $H_{hf}$ (B-자리)=510, $H_{hf}$(A-자리)=475 kOe, 이성질체 이동 값은 0.37(B-자리), 0.33mm/s(A-자리)로 분석되었다. VSM측정 결과로부터 상온에서 초상자성 특성을 갖는 7nm $Zn_{0.5}Ni_{0.5}Fe_2O_4$의 차단온도 $T_B$는 90 K로 결정하였으며, 자기이방성상수 $K=1.6\times10^6\;erg/cm^3$ 값을 얻었다.

Keywords

References

  1. S. H. Im, T. Herricks, Y. T. Lee, and Y. Xia, Chem. Phys. Lett. 401, 19(2005) https://doi.org/10.1016/j.cplett.2004.11.028
  2. Y. Qiang, J. Antony, M. G. Marino, and S. Pendyala, IEEE Trans. Mag. 40, 3538(2004) https://doi.org/10.1109/TMAG.2004.828962
  3. S. Sun and H. Zeng, J. Am. Chem. Soc. 124, 8204(2002) https://doi.org/10.1021/ja026501x
  4. V. Skumryev, S. Stoyanov, Y. Zhang, G Hadjipanayis, D. Givord, and J. Nogue's, Nature 423, 19(2003)
  5. M. Ghosh, G. Lawes, A. Gayen, G. N. Subbanna, W. M. Reiff, M. A. Subramanian, A. P. Ramirez, J. P. Zhang, and R. Seshadri, Chem. Mater. 16, 118(2004) https://doi.org/10.1021/cm030346j
  6. S. W. Lee, K. J. Woo, and C. S. Kim, J. of Magnetics 9, 83(2005)
  7. Q. Chen and Z. J. Zhang, Appl. Phys. Lett. 73, 3156(1998) https://doi.org/10.1063/1.122704
  8. S. Y. An, I. B. Shim, and C. S. Kim, J. Appl. Phys. 97, 10Q909 (2005) https://doi.org/10.1063/1.1851919
  9. S. Roy and J. Ghose, J. Appl. Phys. 87, 6226(2000) https://doi.org/10.1063/1.372662
  10. S. R. Ahmed, S. B. Oga1e, G. C. Papaefthymiou, R. Ramesh, and P. Kofinas, Appl. Phys. Lett. 80, 1616(2002) https://doi.org/10.1063/1.1456258
  11. Y. P. Fu and C. H. Lin, J. Magn. Magn. Mater. 251, 74(2002) https://doi.org/10.1016/S0304-8853(02)00478-X
  12. S. Y. An, I. B. Shim, and C. S. Kim, J. Magn. Magn. Mater. 290, 1551 (2005) https://doi.org/10.1016/j.jmmm.2004.11.244
  13. S. W. Lee, S. Y. An, S. J. Kim, and C. S. Kim, J. Korean Phys. Soc. 48, 75(2006)
  14. Cullity, Introduction to magnetic materials (Addison-Wesley Publshing Co. 1972)
  15. E. J. Choi, Y. G Ahn, S. H. Kim, D. H. An, K. U. Kang, B. G Lee, K. S. Baek, and H. N. Oak, J. Magn. Magn. Mater. 262, L198(2003) https://doi.org/10.1016/S0304-8853(03)00224-5
  16. B. K. Nath, P. K. Chakrabarti, S. Das, U. Kumar, P. K. Mukhopadhyay, and D. Das, Eur. Phys. B 39, 417(2004) https://doi.org/10.1140/epjb/e2004-00212-0
  17. S. W. Lee and C. S. Kim, J. of Magnetics 10, 84(2005) https://doi.org/10.4283/JMAG.2005.10.3.084