Abstract
This article presents the results of experimental study that investigates the effect of filler and shrinkage reducing agent influencing on the strength properties of MMA-modified polymer paste that was produced to develop the surface-repair and coating materials of the concrete structures. Results show that the flexural and compressive strengths of the polymer paste increased 29 and 27%, respectively, when the aluminum hydroxide completely replaced the calcium carbonate as the filler Furthermore, when the shrinkage reducing agent was used 30%, both strengths decreased about 29% comparing to when the agent was not used. As in the cases of flexural and compressive strengths, the adhesive strength increased as the content of aluminum hydroxide as the filler increased, and it decreased as the content of shrinkage reducing agent increased. The adhesive strength with a dry concrete substrate turned out to be $30{\sim}40%$ higher than that with a wet concrete substrate.
본 연구는 콘크리트 구조물의 표면보수 및 코팅재를 개발할 목적으로 충전재 및 수축저감제가 MMA 개질 폴리머 페이스트의 경화수축 및 강도특성에 미치는 영향을 구명한 것이다. 그 결과 수축저감제를 30% 첨가하였을 경우 경화수축이 평균 $14.9{\times}10^{-4}$으로 수축저감제를 사용치 않았을 경우에 비해 약 82%의 수축저감효과를 나타냈으며, 충전재로서 탄산칼슘만 사용했을 경우보다 이를 수산화 알루미늄으로 완전히 대체하였을 때, 휨 및 압축강도는 각각 29%, 27% 증가하였다. 그리고 수축저감제를 30% 사용하면 수축저감제를 사용하지 않은것에 비해 휨 및 압축강도는 약 29% 감소하였다. 한편, 부착강도는 휨 및 압축강도와 마찬가지로 충전재로서 수산화 알루미늄의 비율이 클수록 증가하였으며, 수축저감제를 많이 사용할수록 감소 하였다. 그리고 건조한 바탕 콘크리트를 기준으로 할 때, 습윤한 바탕콘크리트에서의 부착강도는 약 $30{\sim}40%$ 높게 나타났다.