Flowability and Strength Properties of Mortar and Self-Compacting Concrete Mixed with Waste Concrete Powder

폐콘크리트 분말을 혼합한 모르타르 및 자기충전 콘크리트의 유동 및 강도특성

  • Published : 2006.08.31

Abstract

In this study, in order to utilize waste concrete powder(WCP) which is occurred in manufacturing high quality recycled aggregate as an admixture for self-compacting concrete(SCC), the properties of cement paste, mortar, and concrete that were mixed two types of WCP, 928 and 1,360 $cm^2/g$ of surface area, were analyzed. As a result of experiment, we have found that WCP was a porous material with angle. When WCP was utilized as an admixture for SCC, its flowability and viscosity increased in proportion to the increase of a replacement ratio, and that a replacement ratio of WCP was proper within 15%. The compressive strength at 28 days mixed respectively with WCP2, 15 and 30%, showed about 36 and 28 MPa, and it showed a similar trend with a function suggested in CEB-FIP for the relationship of compressive strength and elastic modulus. According to the results, it is judged that WCP2 can be utilized as an mineral admixture of normal strength SCC.

본 연구는 폐콘크리트를 파쇄하여 고품질 재생골재로 제조시 발생되는 폐콘크리트 분말(WCP)을 자기충전 콘크리트(SCC)용 혼화재료로 활용하기 위하여 분말도가 928 및 $1,360cm^2/g$인 2종류의 폐콘크리트 분말(WCP)을 혼합한 시멘트 페이스트, 모르타르 및 콘크리트의 특성들을 분석하였다. 실험결과 폐콘크리트 분말은 각진 형태의 다공성 재료로 자기충전 콘크리트(SCC)용 혼화재료로 활용할 경우 유동성 및 점성은 혼합률이 증가함에 따라 비례적으로 감소하였으며, 자기충전 콘크리트(SCC)의 목표성능기준을 만족하는 혼합률은 15%이내가 적절할 것으로 판단되었다. 폐콘크리트 분말(WCP2)을 15 및 30% 혼합한 재령 28일 압축강도는 약 36 및 28MPa를 나타내었으며, 압축강도와 정탄성계수의 관계에는 CEB-FIP 에서 제시한 함수와 유사한 경향을 나타내었다. 이상의 실험결과, 보통강도용 자기충전 콘크리트(SCC)의 혼화재료로 폐콘크리트 분말(WCP2)을 활용할 수 있을 것으로 판단된다.

Keywords

References

  1. 환경부, 전국 폐기물 발생 및 처리현황, 폐기물통계, 환경부, 2004
  2. 飯田一彦,佐伯龍彦,長瀧重義,'セメントをめたコンクリ-トのリサイクル,' コンクリ-ト工學論文集,第11卷, 第 3號, 2000. 9, pp.139-144
  3. 中野錦ー 'セメント製造はおける省エネの工夫と廃棄物 の利用,' コンクリ-ト 工學, Vol.34, No.10, 1996. 10, pp.82-87
  4. 横山 滋 ,'セメント原料への利用', コンクリ-ト工學, Vol.35, No.7, 1997. 7, pp.49-52
  5. Okamura, H., Self-compacting high performanceconcrete, Social System Institute, Tokyo, 1999
  6. Okamura, H., Maekawa, K., and Ozawa, K., 'High performance concrete.' Gihoudou Pub., Tokvo. 1998
  7. 宮野和樹,桝田佳寛,中村成春,'セメントペ-ストのレオロジ-特性に及ぽす調合要因の影響,' コンクリ-ト工學年次論文集,日本ンクリ-ト工學協會, Vol.22, No.2, 2000, pp.355-361
  8. 呉相均,商流動コンクリートのレオロジ-評慣および流動 設計,東京大學, 1999
  9. Hall, C, 'Water sorptivity of mortars and concretes : a review,' Magazine of Concrete Research, 1989. 6, 41, No.147, pp.51-61 https://doi.org/10.1680/macr.1989.41.147.51
  10. Japan Society of Civil Engineers(JSCE), 高流動 コンクリト-施工指針, JSLE, 2000
  11. Nan, S., Miao, B., 'A new method for the mixdesign of medium strength flowing concrete with low cement content,' Cement and Concrete Composite, Vol. 25, Issue 2, 2003, pp.215-222 https://doi.org/10.1016/S0958-9465(02)00013-6
  12. Nan S., Hsu, K. C., and Chai, H. W., 'A simple mix design method for self-compacting concrete,' Cement and Concrete Research, Vol.31, Issue 12, 2001, pp.1799-1807 https://doi.org/10.1016/S0008-8846(01)00566-X
  13. 최연왕, 정문영, 정지승, 문대중, 안성일, '골재 채움율과 잔골재 용적비를 고려한 자기충전형 콘크리트의 최적 배합', 한국콘크리트학회 가을학술발표회논문집, 한국콘크리트학회, 고려대학교,Vol.14, No.2, 2002, pp.549-554
  14. 문대중, 정문영, 최연왕, '폐콘크리트 분말 사용 모르타르의 역학적 특성', 한국지구시스템공학회지, 2003, Vol.40, No.6 pp.438-445