Abstract
The strength standard of shotcrete in Korea is relatively lower than that in Europe where high-strength shotcrete has been developed and actively applied to the common practice, so it is hard to test a quality of high-strength shotcrete. In this study, field test was performed to find a solution improving the strength and a long-term durability on domestic shotcrete. In field test, a high-strength shotcrete was produced using high-quality additions and accelerators, and an effect of additions and accelerators was observed. In addition, quality test based on EFNARC was also performed. As a result of field test, a promotion ratio of early strength is 90~97% in case of using alkali-free accelerators, therefore, alkali-free accelerators had an effect on an increase of early strength on shotcrete. A compressive strength of shotcrete using Micro-silica fume was 45.2~55.8MPa and flexible strength was 5.01~6.66MPa, so a promotion ratio of strength was 37~79%, 17~61% respectively. It was showed that increment effect of strength by the silica fume replacement of 7.5~10% for cement mass was remarkable. As a result of test, it was possible to apply high-strength shotcrete to the domestic practice using high-quality additions such as Micro-silica fume and accelerators such as alkali-free.
국내 숏크리트 강도기준은 고강도 숏크리트의 개발과 적용이 활발한 유럽과 비교해 볼 때 상대적으로 낮게 설정되어 있어서 고강도 숏크리트의 품질을 평가하기에는 어려움이 있다. 본 연구에서는 국내 숏크리트의 강도증진과 장기 내구성을 향상시킬 수 있는 방법을 모색하기 위해 현장실험을 실시하였다. 현장실험은 고품질 혼화재와 고성능 급결제를 적용한 고강도 숏크리트를 지향하였고, 숏크리트의 강도증진에 미치는 혼화재와 급결제의 영향을 파악하고자 하였다. 그리고 유럽통합규격(EFNARC)에 의거하여 품질평가를 수행하였는데, 실험결과 알칼리프리계 급결제를 사용한 경우의 초기강도 증진율이 90~97%로 가장 높게 나타나 초기강도 증진효과에 알칼리프리계 급결제가 효과적이었다. 또한, 실리카 흄을 혼입한 숏크리트는 압축강도가 45.2~55.8MPa, 휨강도가 5.01~6.66MPa로 혼입하지 않은 경우에 비해 각각 37~79%, 17~61%의 강도증진 효과가 나타났고, 실리카 흄 치환율은 7.5~10%일 때 강도증진 효과가 가장 우수한 것으로 나타났다. 현장실험 결과 국내 숏크리트의 고강도화를 위해서는 알카리프리계 급결제와 실리카 흄과 같은 고품질 혼화재의 사용이 필요할 것으로 판단된다.